Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Shrinkage rate | | 内部方法 | 0.30-0.70 % |
| Shrinkage rate | | 内部方法 | 0.10-0.40 % |
| Water absorption rate | | ISO 62 | 0.020 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | HB |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| elongation at break | | ASTM D638/ISO 527 | 2.1 % |
| tensile strength | | ASTM D638/ISO 527 | 100 kg/cm²(MPa)[Lb/in²] |
| Rockwell hardness | | ASTM D785 | 47 |
| Flexural modulus | | ASTM D790/ISO 178 | 9.8 kg/cm²(MPa)[Lb/in²] |
| bending strength | | ASTM D790/ISO 178 | 165 kg/cm²(MPa)[Lb/in²] |
| Tensile modulus | | ISO 527-2 | 11000 Mpa |
| tensile strength | | ISO 527-2 | 100 Mpa |
| Tensile strain | | ISO 527-2 | 2.1 % |
| Flexural modulus | | ISO 178 | 9800 Mpa |
| bending strength | | ISO 178 | 165 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of simply supported beam without notch | | ISO 179 | 32 kJ/m² |
| Suspended wall beam without notch impact strength | | ISO 180 | 29 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| arc resistance | | ASTM D495/IEC 60112 | 110 |
| Volume resistivity | | ASTM D257/IEC 60093 | >1.0*10^16 Ω.cm |
| Dissipation Factor | | IEC 60250 | <1.0E-3 |
| arc resistance | | ASTM D495 | PLC6 |
| Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | PLC 0 |
| Volume resistivity | | IEC 60093 | >1.0E+16 ohms·cm |
| dielectric strength | | ASTM D149 | 50 KV/mm |
| dielectric constant | | IEC 60250 | 3.40 |
| Physical properties | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D792/ISO 1183 | 1.41 |
| Shrinkage rate | | ASTM D955 | MD 0.1-0.4 % |
| Water absorption rate | | ASTM D570/ISO 62 | 0.02 % |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Linear coefficient of thermal expansion | | ASTM D696/ISO 11359 | MD 2.2 mm/mm.℃ |
| Heat distortion temperature | | ISO 75-2/B | 265 °C |
| Heat distortion temperature | | ISO 75-2/A | 230 °C |
| Linear coefficient of thermal expansion | | TMA | 2.2E-05 cm/cm/°C |
| Linear coefficient of thermal expansion | | TMA | 4.9E-05 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.