Technical Data Sheet
physical property | Test Condition | Test Method | Test Result |
---|
Melt volume flow rate | | ISO 1133 | 9.00 cm³/10min |
Shrinkage rate | | ISO 294-4 | 0.60to0.70 % |
Shrinkage rate | | ISO 294-4 | 0.60to0.70 % |
density | | ISO 1183 | 1.04 g/cm³ |
hardness | Test Condition | Test Method | Test Result |
---|
ball-indentation hardness | | ISO 2039-1 | 105 MPa |
flammability | Test Condition | Test Method | Test Result |
---|
burning rate | | ISO 3795 | <55 mm/min |
UL flame retardant rating | | UL 94 | HB |
Impact resistance | Test Condition | Test Method | Test Result |
---|
Impact strength of cantilever beam gap | | ISO 180/1A | 13 kJ/m² |
Charpy Notched Impact Strength | | ISO 179/1eA | 13 kJ/m² |
Impact strength of cantilever beam gap | | ISO 180/1A | 8.0 kJ/m² |
Mechanical properties | Test Condition | Test Method | Test Result |
---|
Tensile modulus | | ISO 527-2/1 | 2200 MPa |
tensile strength | | ISO 527-2/50 | 42.0 MPa |
Tensile strain | | ISO 527-2/50 | 17 % |
Flexural modulus | | ISO 178 | 2400 MPa |
bending strength | | ISO 178 | 66.0 MPa |
Thermal performance | Test Condition | Test Method | Test Result |
---|
Heat distortion temperature | | ISO 75-2/B | 112 °C |
Heat distortion temperature | | ISO 75-2/A | 104 °C |
vicat | | ISO 306/B50 | 112 °C |
vicat | | ISO 306/B120 | 114 °C |
Linear coefficient of thermal expansion | | ISO 11359-2 | 9.2E-05 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.