ABS ELIX™ ABS HH 3114 ELIX Polymers, S. L.
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Impact resistance | Test Condition | Test Method | ELIX Polymers, S. L./ELIX™ ABS HH 3114 |
---|---|---|---|
Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 13 kJ/m² |
Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 8.0 kJ/m² |
23°C | ISO 180/1A | 13 kJ/m² |
hardness | Test Condition | Test Method | ELIX Polymers, S. L./ELIX™ ABS HH 3114 |
---|---|---|---|
ball-indentation hardness | ISO 2039-1 | 105 MPa |
Mechanical properties | Test Condition | Test Method | ELIX Polymers, S. L./ELIX™ ABS HH 3114 |
---|---|---|---|
tensile strength | 屈服,23°C | ISO 527-2/50 | 42.0 MPa |
Flexural modulus | 23°C | ISO 178 | 2400 MPa |
Tensile strain | 断裂,23°C | ISO 527-2/50 | 17 % |
Tensile modulus | 23°C | ISO 527-2/1 | 2200 MPa |
bending strength | 23°C | ISO 178 | 66.0 MPa |
flammability | Test Condition | Test Method | ELIX Polymers, S. L./ELIX™ ABS HH 3114 |
---|---|---|---|
burning rate | 2.00mm | ISO 3795 | <55 mm/min |
UL flame retardant rating | 1.6mm | UL 94 | HB |
physical property | Test Condition | Test Method | ELIX Polymers, S. L./ELIX™ ABS HH 3114 |
---|---|---|---|
Melt volume flow rate | 220°C/10.0kg | ISO 1133 | 9.00 cm³/10min |
Shrinkage rate | TD | ISO 294-4 | 0.60to0.70 % |
MD | ISO 294-4 | 0.60to0.70 % | |
density | ISO 1183 | 1.04 g/cm³ |
Thermal performance | Test Condition | Test Method | ELIX Polymers, S. L./ELIX™ ABS HH 3114 |
---|---|---|---|
vicat | -- | ISO 306/B120 | 114 °C |
Linear coefficient of thermal expansion | MD:23到55°C | ISO 11359-2 | 9.2E-05 cm/cm/°C |
Heat distortion temperature | 1.8MPa,退火,HDT | ISO 75-2/A | 104 °C |
vicat | -- | ISO 306/B50 | 112 °C |
Heat distortion temperature | 0.45MPa,退火,HDT | ISO 75-2/B | 112 °C |