Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Shrinkage rate | | 内部方法 | 1.2to1.6 % |
| Water absorption rate | | ASTMD570 | 0.080 % |
| Water absorption rate | | ISO62 | 0.50 % |
| Water absorption rate | | ISO62 | 0.15 % |
| Outdoor applicability | | UL746C | f2 |
| density | | ASTMD792 | 1.35 g/cm³ |
| Specific volume | | ASTMD792 | 0.740 cm³/g |
| density | | ISO1183 | 1.34 g/cm³ |
| melt mass-flow rate | | ASTMD1238 | 9.6 g/10min |
| Melt volume flow rate | | ISO1133 | 8.00 cm3/10min |
| Shrinkage rate | | 内部方法 | 0.80to1.1 % |
| Shrinkage rate | | 内部方法 | 1.0to1.4 % |
| Shrinkage rate | | 内部方法 | 1.0to1.4 % |
| Shrinkage rate | | 内部方法 | 0.90to1.3 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | ASTMD785 | 117 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL94 | HB |
| UL flame retardant rating | | UL94 | V-0 |
| UL flame retardant rating | | UL94 | 5VA |
| Burning wire flammability index | | IEC60695-2-12 | 960 °C |
| Hot filament ignition temperature | | IEC60695-2-13 | 775 °C |
| Hot filament ignition temperature | | IEC60695-2-13 | 750 °C |
| Hot filament ignition temperature | | IEC60695-2-13 | 725 °C |
| Limiting Oxygen Index | | ASTMD2863 | 30 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile stress | | ISO527-2/50 | 40.0 Mpa |
| Tensile strain 5 | | ASTMD638 | 5.0 % |
| Tensile strain | | ISO527-2/50 | 5.0 % |
| Tensile strain 5 | | ASTMD638 | 54 % |
| Tensile strain | | ISO527-2/50 | 30 % |
| Bending modulus 7 | | ASTMD790 | 2100 Mpa |
| Bending modulus 7 | | ISO178 | 2000 Mpa |
| | ISO178 | 73.0 Mpa |
| Bending strength 7 | | ASTMD790 | 78.0 Mpa |
| Flexural Strength6 | | ASTMD790 | 78.0 Mpa |
| Tensile modulus 4 | | ASTMD638 | 2020 Mpa |
| Tensile modulus | | ISO527-2/1 | 2200 Mpa |
| Tensile strength 6 | | ASTMD638 | 48.0 Mpa |
| Tensile stress | | ISO527-2/50 | 50.0 Mpa |
| Tensile strength 5 | | ASTMD638 | 42.0 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| CharpyNotchedImpactStrength9 | | ISO179/1eA | 45 kJ/m² |
| Impact strength of cantilever beam gap | | ASTMD256 | 150 J/m |
| Impact strength of cantilever beam gap | | ASTMD256 | 320 J/m |
| Suspended wall beam gap impact strength 10 | | ISO180/1A | 10 kJ/m² |
| Suspended wall beam gap impact strength 10 | | ISO180/1A | 45 kJ/m² |
| Impact strength of cantilever beam gap | | ASTMD4812 | NoBreak |
| Dart impact equipped with measuring instruments | | ASTMD3763 | 35.8 J |
| Falling hammer impact | | ASTMD3029 | 43.4 J |
| Falling hammer impact | | ASTMD3029 | 43.0 J |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Volume resistivity | | ASTMD257 | >1.2E+16 ohms·cm |
| dielectric strength | | ASTMD149 | 25 KV/mm |
| dielectric strength | | ASTMD149 | 19 KV/mm |
| dielectric strength | | ASTMD149 | 19 KV/mm |
| dielectric constant | | ASTMD150 | 3.20 |
| dielectric constant | | ASTMD150 | 3.20 |
| Dissipation Factor | | ASTMD150 | 3E-03 |
| Dissipation Factor | | ASTMD150 | 0.030 |
| Arc resistance 15 | | ASTMD495 | PLC6 |
| Compared to the Leakage Tracking Index (CTI) | | UL746 | PLC 2 |
| High arc combustion index (HAI) | | UL746 | PLC 3 |
| High Voltage Arc Traceability Rate (HVTR) | | UL746 | PLC 3 |
| Hot wire ignition (HWI) | | UL746 | PLC 2 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ASTMD648 | 135 °C |
| Heat distortion temperature | | ASTMD648 | 138 °C |
| Heat distortion temperature | | ASTMD648 | 98.0 °C |
| Heat distortion temperature | | ASTMD648 | 99.0 °C |
| | ISO75-2/Af | 84.0 °C |
| vicat | | ASTMD152513 | 134 °C |
| vicat | | ISO306/B50 | 145 °C |
| vicat | | ISO306/B120 | 150 °C |
| BallPressure Test14 | | IEC60695-10-2 | Pass |
| | ASTME831 | 9.2E-05 cm/cm/°C |
| | ASTME831 | 1.2E-04 cm/cm/°C |
| | ISO11359-2 | 7.2E-05 cm/cm/°C |
| | ASTME831 | 8.4E-05 cm/cm/°C |
| | ISO11359-2 | 8.4E-05 cm/cm/°C |
| RTI Elec | | UL746 | 120 °C |
| RTI Imp | | UL746 | 120 °C |
| RTI Str | | UL746 | 140 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.