PBT/PC 357-1001 SABIC INNOVATIVE SHANGHAI
VALOX™ 
switch、Shell、Roller、Spool
UV resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Impact resistanceTest ConditionTest MethodSABIC INNOVATIVE SHANGHAI/357-1001
Impact strength of cantilever beam gap23°CASTMD256320 J/m
Falling hammer impact23°C11ASTMD302943.0 J
23°CASTMD302943.4 J
Suspended wall beam gap impact strength 1023°CISO180/1A45 kJ/m²
-30°CISO180/1A10 kJ/m²
Impact strength of cantilever beam gap23°CASTMD4812NoBreak
CharpyNotchedImpactStrength923°CISO179/1eA45 kJ/m²
Impact strength of cantilever beam gap-30°CASTMD256150 J/m
Dart impact equipped with measuring instruments23°C,TotalEnergyASTMD376335.8 J
hardnessTest ConditionTest MethodSABIC INNOVATIVE SHANGHAI/357-1001
Rockwell hardnessR级ASTMD785117
Mechanical propertiesTest ConditionTest MethodSABIC INNOVATIVE SHANGHAI/357-1001
Tensile stress屈服ISO527-2/5050.0 Mpa
Tensile strain 5YieldASTMD6385.0 %
Bending modulus 7ISO1782000 Mpa
50.0mm跨距ASTMD7902100 Mpa
Tensile strain屈服ISO527-2/505.0 %
Tensile stress断裂ISO527-2/5040.0 Mpa
Tensile strain 5BreakASTMD63854 %
Tensile strength 5BreakASTMD63842.0 Mpa
Tensile modulusISO527-2/12200 Mpa
Tensile strength 6屈服ASTMD63848.0 Mpa
Bending strength 7屈服,50.0mm跨距ASTMD79078.0 Mpa
Tensile strain断裂ISO527-2/5030 %
Flexural Strength6Break,50.0mmSpanASTMD79078.0 Mpa
ISO17873.0 Mpa
Tensile modulus 4ASTMD6382020 Mpa
Electrical performanceTest ConditionTest MethodSABIC INNOVATIVE SHANGHAI/357-1001
High arc combustion index (HAI)HAIUL746PLC 3
Volume resistivityASTMD257>1.2E+16 ohms·cm
dielectric constant100HzASTMD1503.20
Dissipation Factor100HzASTMD1503E-03
dielectric constant1MHzASTMD1503.20
dielectric strength1.60mm,在油中ASTMD14925 KV/mm
3.20mm,在油中ASTMD14919 KV/mm
Compared to the Leakage Tracking Index (CTI)CTIUL746PLC 2
Arc resistance 15ASTMD495PLC6
High Voltage Arc Traceability Rate (HVTR)HVTRUL746PLC 3
Hot wire ignition (HWI)HWIUL746PLC 2
dielectric strength3.20mm,inAirASTMD14919 KV/mm
Dissipation Factor1MHzASTMD1500.030
flammabilityTest ConditionTest MethodSABIC INNOVATIVE SHANGHAI/357-1001
UL flame retardant rating0.63mmUL94V-0
Limiting Oxygen IndexASTMD286330 %
Burning wire flammability index1.0mmIEC60695-2-12960 °C
Hot filament ignition temperature3.0mmIEC60695-2-13725 °C
UL flame retardant rating3.0mmUL945VA
Hot filament ignition temperature1.0mmIEC60695-2-13775 °C
2.0mmIEC60695-2-13750 °C
UL flame retardant rating0.46mmUL94HB
physical property Test ConditionTest MethodSABIC INNOVATIVE SHANGHAI/357-1001
Shrinkage rateMD：3.20mm内部方法1.0to1.4 %
MD：--2内部方法0.80to1.1 %
MD：--3内部方法1.0to1.4 %
Outdoor applicabilityUL746Cf2
Shrinkage rateTD：--2内部方法0.90to1.3 %
TD：--3内部方法1.2to1.6 %
Water absorption rate平衡,23°C,50%RHISO620.15 %
melt mass-flow rate250°C/5.0kgASTMD12389.6 g/10min
Water absorption rate饱和,23°CISO620.50 %
densityASTMD7921.35 g/cm³
Melt volume flow rate250°C/5.0kgISO11338.00 cm3/10min
Water absorption rate24hrASTMD5700.080 %
densityISO11831.34 g/cm³
Specific volumeASTMD7920.740 cm³/g
Thermal performanceTest ConditionTest MethodSABIC INNOVATIVE SHANGHAI/357-1001
Heat distortion temperature0.45MPa,未退火,3.20mmASTMD648135 °C
MD：-40到40°CISO11359-27.2E-05 cm/cm/°C
TD：-40到40°CISO11359-28.4E-05 cm/cm/°C
Heat distortion temperature1.8MPa,未退火,6.40mmASTMD64899.0 °C
1.8MPa,Unannealed,64.0mmSpanISO75-2/Af84.0 °C
MD：60to138°CASTME8311.2E-04 cm/cm/°C
Heat distortion temperature0.45MPa,未退火,6.40mmASTMD648138 °C
vicat--ISO306/B50145 °C
RTI ImpUL746120 °C
vicatASTMD152513134 °C
MD：-40to40°CASTME8319.2E-05 cm/cm/°C
RTI StrUL746140 °C
RTI ElecUL746120 °C
BallPressure Test14125°CIEC60695-10-2Pass
Heat distortion temperature1.8MPa,未退火,3.20mmASTMD64898.0 °C
vicat--ISO306/B120150 °C
TD：-40到40°CASTME8318.4E-05 cm/cm/°C