PP TRANSMARE® 14CT20-0.002

Properties:
Filler
talc filler
20%
filler by weight
Compare

Technical Data Sheet

physical property	Test Condition	Test Method	Test Result
density		ISO 1183	1.05 g/cm³
melt mass-flow rate		ISO 1133	15 g/10min
melt mass-flow rate	melt mass-flow rate		ISO 1133	60 g/10min

hardness	Test Condition	Test Method	Test Result
Shore hardness		ISO 868	61

Mechanical properties	Test Condition	Test Method	Test Result
Tensile strain		ISO 527-2/50	50 %
Flexural modulus		ISO 178	2000 MPa
bending strength		ISO 178	33.0 MPa
tensile strength		ISO 527-2/50	21.0 MPa
tensile strength	tensile strength		ISO 527-2/50	16.0 MPa
Tensile strain		ISO 527-2/50	3.5 %

Impact resistance	Test Condition	Test Method	Test Result
Charpy Notched Impact Strength		ISO 179/A	2.5 kJ/m²
	Charpy Notched Impact Strength		ISO 179/A	4.0 kJ/m²
		Charpy Notched Impact Strength		ISO 179/A	5.7 kJ/m²
		Charpy Notched Impact Strength	Charpy Notched Impact Strength		ISO 179/A	8.0 kJ/m²
Impact strength of cantilever beam gap		ISO 180/A	3.5 kJ/m²
	Impact strength of cantilever beam gap		ISO 180/A	4.5 kJ/m²
		Impact strength of cantilever beam gap		ISO 180/A	6.5 kJ/m²
		Impact strength of cantilever beam gap	Impact strength of cantilever beam gap		ISO 180/A	11 kJ/m²

Thermal performance	Test Condition	Test Method	Test Result
vicat		ISO 306/A	143 °C
Heat distortion temperature		ISO 75-2/B	81.0 °C
Heat distortion temperature	Heat distortion temperature		ISO 75-2/A	54.0 °C

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.