Impact resistance | Test Condition | Test Method | Transmare Compounding B.V./TRANSMARE® 14CT20-0.002 |
---|---|---|---|
Charpy Notched Impact Strength | -20°C | ISO 179/A | 4.0 kJ/m² |
-40°C | ISO 179/A | 2.5 kJ/m² | |
Impact strength of cantilever beam gap | 0°C | ISO 180/A | 6.5 kJ/m² |
Charpy Notched Impact Strength | 0°C | ISO 179/A | 5.7 kJ/m² |
23°C | ISO 179/A | 8.0 kJ/m² | |
Impact strength of cantilever beam gap | -40°C | ISO 180/A | 3.5 kJ/m² |
23°C | ISO 180/A | 11 kJ/m² | |
-20°C | ISO 180/A | 4.5 kJ/m² |
hardness | Test Condition | Test Method | Transmare Compounding B.V./TRANSMARE® 14CT20-0.002 |
---|---|---|---|
Shore hardness | 邵氏D | ISO 868 | 61 |
Mechanical properties | Test Condition | Test Method | Transmare Compounding B.V./TRANSMARE® 14CT20-0.002 |
---|---|---|---|
tensile strength | 断裂,4.00mm | ISO 527-2/50 | 16.0 MPa |
Tensile strain | 断裂,4.00mm | ISO 527-2/50 | 50 % |
Flexural modulus | ISO 178 | 2000 MPa | |
tensile strength | 屈服,4.00mm | ISO 527-2/50 | 21.0 MPa |
Tensile strain | Yield,4.00mm | ISO 527-2/50 | 3.5 % |
bending strength | ISO 178 | 33.0 MPa |
physical property | Test Condition | Test Method | Transmare Compounding B.V./TRANSMARE® 14CT20-0.002 |
---|---|---|---|
density | ISO 1183 | 1.05 g/cm³ | |
melt mass-flow rate | 230°C/5.0kg | ISO 1133 | 60 g/10min |
230°C/2.16kg | ISO 1133 | 15 g/10min |
Thermal performance | Test Condition | Test Method | Transmare Compounding B.V./TRANSMARE® 14CT20-0.002 |
---|---|---|---|
Heat distortion temperature | 0.45MPa,未退火,HDT | ISO 75-2/B | 81.0 °C |
1.8MPa,未退火,HDT | ISO 75-2/A | 54.0 °C | |
vicat | ISO 306/A | 143 °C |