Technical Data Sheet
physical property | Test Condition | Test Method | Test Result |
---|
density | | ISO 1183 | 1.22 g/cm³ |
Melt volume flow rate | | ISO 1133 | 13.0 cm³/10min |
Shrinkage rate | | 内部方法 | 0.70to1.0 % |
Water absorption rate | | ISO 62 | 0.50 % |
Water absorption rate | | ISO 62 | 0.15 % |
Impact resistance | Test Condition | Test Method | Test Result |
---|
Impact strength of cantilever beam gap | | ISO 180/1A | 35 kJ/m² |
Impact strength of cantilever beam gap | | ISO 180/1A | 40 kJ/m² |
Charpy Notched Impact Strength | | ISO 179/1eA | 15 kJ/m² |
Charpy Notched Impact Strength | | ISO 179/1eA | 40 kJ/m² |
Charpy Notched Impact Strength | | ISO 179/1eA | 50 kJ/m² |
Impact strength of simply supported beam without notch | | ISO 179/1eU | 无断裂 |
Impact strength of cantilever beam gap | | ISO 180/1A | 18 kJ/m² |
Impact strength of cantilever beam gap | | ISO 180/1A | 20 kJ/m² |
Impact strength of cantilever beam gap | | ISO 180/1A | 45 kJ/m² |
Mechanical properties | Test Condition | Test Method | Test Result |
---|
Flexural modulus | | ISO 178 | 2050 MPa |
bending strength | | ISO 178 | 80.0 MPa |
Tensile modulus | | ISO 527-2/1 | 2150 MPa |
tensile strength | Yield | ISO 527-2/50 | 54.0 MPa |
tensile strength | Break | ISO 527-2/50 | 40.0 MPa |
Tensile strain | Yield | ISO 527-2/50 | 4.5 % |
Tensile strain | Break | ISO 527-2/50 | 50 % |
Filling analysis | Test Condition | Test Method | Test Result |
---|
melt viscosity | | ISO 11443 | 215 Pa·s |
Thermal performance | Test Condition | Test Method | Test Result |
---|
Linear coefficient of thermal expansion | | ISO 11359-2 | 8.5E-05 cm/cm/°C |
Linear coefficient of thermal expansion | | ISO 11359-2 | 8E-05 cm/cm/°C |
thermal conductivity | | ISO 8302 | 0.20 W/m/K |
ball-indentation hardness | | IEC 60695-10-2 | Pass |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.