Material Comparison

Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC+Polyester XENOY™ X5100 resin SABIC
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Impact resistanceTest ConditionTest MethodSABIC/XENOY™ X5100 resin
Charpy Notched Impact Strength0°C5ISO 179/1eA40 kJ/m²
Impact strength of simply supported beam without notch-30°CISO 179/1eU无断裂
Impact strength of cantilever beam gap-20°CISO 180/1A20 kJ/m²
-30°CISO 180/1A18 kJ/m²
-10°CISO 180/1A35 kJ/m²
Charpy Notched Impact Strength-30°C4ISO 179/1eA15 kJ/m²
Impact strength of cantilever beam gap23°CISO 180/1A45 kJ/m²
Charpy Notched Impact Strength23°C6ISO 179/1eA50 kJ/m²
Impact strength of cantilever beam gap0°CISO 180/1A40 kJ/m²
Mechanical propertiesTest ConditionTest MethodSABIC/XENOY™ X5100 resin
Flexural modulusISO 1782050 MPa
Tensile strain断裂ISO 527-2/5050 %
Tensile modulusISO 527-2/12150 MPa
Tensile strain屈服ISO 527-2/504.5 %
bending strengthISO 17880.0 MPa
tensile strength 屈服ISO 527-2/5054.0 MPa
断裂ISO 527-2/5040.0 MPa
Filling analysisTest ConditionTest MethodSABIC/XENOY™ X5100 resin
melt viscosity260°C,1500sec^-1ISO 11443215 Pa·s
physical property Test ConditionTest MethodSABIC/XENOY™ X5100 resin
Water absorption rate平衡,23°C,50%RHISO 620.15 %
饱和,23°CISO 620.50 %
densityISO 11831.22 g/cm³
Melt volume flow rate250°C/2.16kgISO 113313.0 cm³/10min
Shrinkage rateMD1内部方法0.70to1.0 %
Thermal performanceTest ConditionTest MethodSABIC/XENOY™ X5100 resin
thermal conductivityISO 83020.20 W/m/K
ball-indentation hardness75°CIEC 60695-10-2Pass
Linear coefficient of thermal expansionMD:23到80°CISO 11359-28.5E-05 cm/cm/°C
TD:-40到40°CISO 11359-28E-05 cm/cm/°C