ABS Stylac™ VA518
37
- Properties:Flame retardant
- Certificates:UL
CompareTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melt mass-flow rate | ISO 1133 | 58 g/10min | |
| Melt volume flow rate | ISO 1133 | 58.0 cm3/10min | |
| Shrinkage rate | ASTM D955 | 0.40-0.60 % |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | UL 94 | V-0 | |
| UL 94 | 5VA |
| Basic performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melt mass-flow rate | JIS K-7210 | 8 g/10min |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| tensile strength | ISO 527-2/50 | 41.8 Mpa | |
| Flexural modulus | ISO 178 | 2400 Mpa | |
| bending strength | ISO 178 | 70.5 Mpa | |
| tensile strength | ASTM D-638 | 39 Mpa | |
| elongation at break | ASTM D-638 | 15 % | |
| bending strength | ASTM D-790 | 69 Mpa | |
| Flexural modulus | ASTM D-790 | 2548 Mpa | |
| Impact strength of cantilever beam gap | ASTM D-256 | 59 J/m |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat distortion temperature | ISO 75-2/A | 74.4 °C | |
| vicat | ISO 306/B | 89.9 °C | |
| RTI Elec | UL 746 | 60.0 °C | |
| RTI Imp | UL 746 | 60.0 °C | |
| RTI | UL 746 | 60.0 °C | |
| Heat distortion temperature | ASTM D-648 | 80 °C | |
| ASTM D-648 | 85 °C | ||
| vicat | ASTM D-1525 | 100 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.