Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
ABS VA518 ASAHI JAPAN
Stylac™
--
Flame retardant
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Basic performance | Test Condition | Test Method | ASAHI JAPAN/VA518 |
|---|---|---|---|
| melt mass-flow rate | JIS K-7210 | 8 g/10min |
| Mechanical properties | Test Condition | Test Method | ASAHI JAPAN/VA518 |
|---|---|---|---|
| tensile strength | 屈服 | ISO 527-2/50 | 41.8 Mpa |
| bending strength | ISO 178 | 70.5 Mpa | |
| Flexural modulus | ISO 178 | 2400 Mpa | |
| ASTM D-790 | 2548 Mpa | ||
| bending strength | ASTM D-790 | 69 Mpa | |
| Impact strength of cantilever beam gap | ASTM D-256 | 59 J/m | |
| tensile strength | ASTM D-638 | 39 Mpa | |
| elongation at break | ASTM D-638 | 15 % |
| flammability | Test Condition | Test Method | ASAHI JAPAN/VA518 |
|---|---|---|---|
| UL flame retardant rating | 2.0mm | UL 94 | 5VA |
| 1.5mm | UL 94 | V-0 |
| physical property | Test Condition | Test Method | ASAHI JAPAN/VA518 |
|---|---|---|---|
| Shrinkage rate | MD | ASTM D955 | 0.40-0.60 % |
| Melt volume flow rate | 220°C/10.0kg | ISO 1133 | 58.0 cm3/10min |
| melt mass-flow rate | 220°C/10.0kg | ISO 1133 | 58 g/10min |
| Thermal performance | Test Condition | Test Method | ASAHI JAPAN/VA518 |
|---|---|---|---|
| vicat | ISO 306/B | 89.9 °C | |
| Heat distortion temperature | 12.7mm，HDT | ASTM D-648 | 85 °C |
| vicat | ASTM D-1525 | 100 °C | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 74.4 °C |
| RTI Imp | UL 746 | 60.0 °C | |
| Heat distortion temperature | 6.4mm，HDT | ASTM D-648 | 80 °C |
| RTI | UL 746 | 60.0 °C | |
| RTI Elec | UL 746 | 60.0 °C |