| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTMD792 | 1.23 g/cm³ |
| melt mass-flow rate | | ASTMD1238 | 18 g/10min |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | R-Scale | ASTMD785 | 120 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL94 | V-0 |
| Burning wire flammability index | | IEC60695-2-12 | 960 °C |
| Hot filament ignition temperature | | IEC60695-2-13 | 775 °C |
| Limiting Oxygen Index | | ASTMD2863 | 37 % |
| UL flame retardant rating | | UL94 | V-1 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| bending strength | | ASTMD790 | 89.6 MPa |
| tensile strength | | ASTMD638 | 62.1 MPa |
| elongation | | ASTMD638 | 75 % |
| Flexural modulus | | ASTMD790 | 2210 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTMD256 | 530 J/m |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| arc resistance | | ASTMD495 | 60.0到120 sec |
| arc resistance | | ASTMD495 | PLC6 |
| Compared to the Leakage Tracking Index (CTI) | | UL746 | 250到400 V |
| Compared to the Leakage Tracking Index (CTI) | | UL746 | PLC 2 |
| High arc combustion index (HAI) | | UL746 | >120 |
| Hot wire ignition (HWI) | | UL746 | 30到60 sec |
| Hot wire ignition (HWI) | | UL746 | PLC 3 |
| Hot wire ignition (HWI) | | UL746 | PLC 2 |
| High arc combustion index (HAI) | | UL746 | 60.0到120 |
| High arc combustion index (HAI) | | UL746 | PLC 0 |
| High arc combustion index (HAI) | | UL746 | PLC 1 |
| High Voltage Arc Traceability Rate (HVTR) | | UL746 | 80.0到150 mm/min |
| High Voltage Arc Traceability Rate (HVTR) | | UL746 | PLC 3 |
| Hot wire ignition (HWI) | | UL746 | 15到30 sec |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat Deflection Temperature | | ASTMD648 | 121 °C |
| Heat Deflection Temperature | | ISO75-2/A | 137 °C |
| RTI | | UL746 | 125 °C |
| Linear thermal expansion coefficient | | ASTME831 | 7E-05 cm/cm/°C |
| Linear thermal expansion coefficient | | ASTME831 | 6.8E-05 cm/cm/°C |
| RTI Elec | | UL746 | 125 °C |
| RTI Imp | | UL746 | 115 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.