PC TRISTAR® PC-10FR-(18) PTS USA
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | PTS USA/TRISTAR® PC-10FR-(18) |
|---|---|---|---|
| Impact strength of cantilever beam gap | 3.17mm | ASTM D256 | 530 J/m |
| hardness | Test Condition | Test Method | PTS USA/TRISTAR® PC-10FR-(18) |
|---|---|---|---|
| Rockwell hardness | R级 | ASTM D785 | 120 |
| Mechanical properties | Test Condition | Test Method | PTS USA/TRISTAR® PC-10FR-(18) |
|---|---|---|---|
| Flexural modulus | 3.17mm | ASTM D790 | 2210 MPa |
| tensile strength | 屈服,3.17mm | ASTM D638 | 62.1 MPa |
| bending strength | 屈服,3.17mm | ASTM D790 | 89.6 MPa |
| elongation | 断裂,3.17mm | ASTM D638 | 75 % |
| Electrical performance | Test Condition | Test Method | PTS USA/TRISTAR® PC-10FR-(18) |
|---|---|---|---|
| Hot wire ignition (HWI) | 3.00mm | UL 746 | PLC 1 sec |
| 1.50mm | UL 746 | PLC 2 sec | |
| 1.5mm | UL 746 | PLC 3 | |
| High arc combustion index (HAI) | 1.5mm | UL 746 | PLC 0 |
| Hot wire ignition (HWI) | 3.0mm | UL 746 | PLC 2 |
| High arc combustion index (HAI) | 3.0mm | UL 746 | PLC 1 |
| arc resistance | ASTM D495 | 60.0to120 sec | |
| High Voltage Arc Traceability Rate (HVTR) | HVTR | UL 746 | PLC 3 |
| High arc combustion index (HAI) | 3.00mm | UL 746 | PLC 0 |
| High Voltage Arc Traceability Rate (HVTR) | HVTR | UL 746 | PLC 4 mm/min |
| arc resistance | ASTM D495 | PLC6 | |
| Compared to the Leakage Tracking Index (CTI) | CTI | UL 746 | PLC 2 |
| High arc combustion index (HAI) | 1.50mm | UL 746 | PLC 0 |
| flammability | Test Condition | Test Method | PTS USA/TRISTAR® PC-10FR-(18) |
|---|---|---|---|
| Hot filament ignition temperature | IEC 60695-2-13 | 775 °C | |
| UL flame retardant rating | 3.0mm | UL 94 | V-0 |
| Burning wire flammability index | IEC 60695-2-12 | 960 °C | |
| UL flame retardant rating | 1.5mm | UL 94 | V-1 |
| Limiting Oxygen Index | ASTM D2863 | 37 % |
| physical property | Test Condition | Test Method | PTS USA/TRISTAR® PC-10FR-(18) |
|---|---|---|---|
| density | ASTM D792 | 1.23 g/cm³ | |
| melt mass-flow rate | 300°C/1.2kg | ASTM D1238 | 18 g/10min |
| Thermal performance | Test Condition | Test Method | PTS USA/TRISTAR® PC-10FR-(18) |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648 | 121 °C |
| Linear coefficient of thermal expansion | TD:-40到95°C | ASTME831 | 6.8E-05 cm/cm/°C |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 137 °C |
| Linear coefficient of thermal expansion | MD:-40到95°C | ASTME831 | 7E-05 cm/cm/°C |
| RTI Imp | UL 746 | 115 °C | |
| RTI | UL 746 | 125 °C | |
| RTI Elec | UL 746 | 125 °C |