| physical property | Test Condition | Test Method | Test Result |
|---|
| melt mass-flow rate | | ASTM D1238 | 1.0 g/10min |
| optical performance | Test Condition | Test Method | Test Result |
|---|
| Haze ratio | | ASTM D-1003 | 18 % |
| gloss | | ASTM D-2457 | 42 |
| gloss | | ASTM D2457 | 39 |
| Haze ratio | | ASTM D1003 | 18 % |
| Basic performance | Test Condition | Test Method | Test Result |
|---|
| melt mass-flow rate | | ASTM D-1238 | 1 g/10min |
| density | | ExxonMobil Method | 0.918 g/cm³ |
| Other performance | Test Condition | Test Method | Test Result |
|---|
| PPA | | | 有 |
| antiblocking agent | | | 否 |
| slip agent | | | 否 |
| thermal stability | | | 有 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | | ASTM D-882 | 9 Mpa |
| tensile strength | | ASTM D-882 | 9.7 Mpa |
| tensile strength | | ASTM D-882 | 75.8 Mpa |
| tensile strength | | ASTM D-882 | 62.7 Mpa |
| elongation at break | | ASTM D-882 | 500 % |
| elongation at break | | ASTM D-882 | 700 % |
| Secant modulus | | ASTM D-882 | 183 Mpa |
| Secant modulus | | ASTM D-882 | 205 Mpa |
| Dart impact | | ASTM D-1709A | 560 g |
| Elmendorf tear strength | | ASTM D-1922 | 280 g |
| Elmendorf tear strength | | ASTM D-1922 | 460 g |
| Puncture Resistance | | ExxonMobil Method | 4.3 J |
| film | Test Condition | Test Method | Test Result |
|---|
| Secant modulus -1% Decant, MD | | ASTM D882 | 185 Mpa |
| Secant modulus -1% Decant, TD | | ASTM D882 | 192 Mpa |
| tensile strength | | ASTM D882 | 9.37 Mpa |
| tensile strength | | ASTM D882 | 9.40 Mpa |
| tensile strength | | ASTM D882 | 54.3 Mpa |
| tensile strength | | ASTM D882 | 42.7 Mpa |
| elongation | | ASTM D882 | 500 % |
| Tensile strain | | ASTM D882 | 600 % |
| Dart impact | | ASTM D1709A | 460 g |
| Elmendorf tear strength | | ASTM D1922 | 250 g |
| Elmendorf tear strength | | ASTM D1922 | 470 g |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Melt Temperature | | ExxonMobil Method | 119 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.