Technical Data Sheet
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | R-Scale | ASTM D785 | 111 |
| Rockwell hardness | R-Scale | ISO 2039-2 | 111 |
| thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat Deflection Temperature | 0.45MPa,未退火,6.40mm | ASTM D648 | 250 °C |
| Heat Deflection Temperature | 0.45MPa,Unannealed,4.00mm | ISO 75-2/B | 250 °C |
| Heat Deflection Temperature | 1.8MPa,未退火,6.40mm | ASTM D648 | 202 °C |
| Heat Deflection Temperature | 1.8MPa,Unannealed,4.00mm | ISO 75-2/A | 202 °C |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | 1.530mm | UL 94 | HB |
| Physical properties | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D792 | 1.77 g/cm³ |
| density | | ISO 1183 | 1.77 g/cm³ |
| melt mass-flow rate | 300°C/2.16kg | ASTM D1238 | 15 g/10min |
| melt mass-flow rate | 300°C/2.16kg | ISO 1133 | 15 g/10min |
| shrinkage rate | MD：3.20mm | ASTM D955 | 0.54 % |
| shrinkage rate | TD：3.20mm | ASTM D955 | 0.56 % |
| shrinkage rate | TD:3.20mm | ISO 2577 | 0.56 % |
| shrinkage rate | MD:3.20mm | ISO 2577 | 0.54 % |
| ash content | -- | ISO 3451 | 51 % |
| ash content | -- | ASTM D5630 | 51 % |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile modulus | | ASTM D638 | 4060 MPa |
| tensile modulus | | ISO 527-2/5 | 4100 MPa |
| tensile strength | Yield | ASTM D638 | 58.8 MPa |
| tensile strength | Yield | ISO 527-2/5 | 56.0 MPa |
| tensile strength | Break | ASTM D638 | 58.8 MPa |
| tensile strength | Break | ISO 527-2/5 | 56.0 MPa |
| elongation | Break | ASTM D638 | 2.1 % |
| bending strength | | ASTM D790 | 90.2 MPa |
| bending strength | | ISO 178 | 80.0 MPa |
| Tensile strain | Break | ISO 527-2/5 | 2.1 % |
| flexural modulus | | ASTM D790 | 6080 MPa |
| flexural modulus | | ISO 178 | 5200 MPa |
| impact performance | Test Condition | Test Method | Test Result |
|---|
| Suspended wall beam without notch impact strength | -5°C | ISO 180/1U | 16 kJ/m² |
| Impact strength of cantilever beam gap | 23°C,6.35mm | ASTM D256 | 27 J/m |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 3.6 kJ/m² |
| Impact strength of cantilever beam gap | 23°C,3.18mm | ASTM D256 | 250 J/m |
| Impact strength of cantilever beam gap | 23°C,6.35mm | ASTM D256 | 200 J/m |
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 20 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 22 kJ/m² |
| Impact strength of cantilever beam gap | 23°C,3.18mm | ASTM D256 | 29 J/m |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare