Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PCT Infino TK-2050HL LOTTE KOREA
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | LOTTE KOREA/Infino TK-2050HL |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 20 kJ/m² |
| Impact strength of cantilever beam gap | 23°C,6.35mm | ASTM D256 | 200 J/m |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 22 kJ/m² |
| Suspended wall beam without notch impact strength | -5°C | ISO 180/1U | 16 kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 3.6 kJ/m² |
| 23°C,3.18mm | ASTM D256 | 29 J/m |
| hardness | Test Condition | Test Method | LOTTE KOREA/Infino TK-2050HL |
|---|---|---|---|
| Rockwell hardness | R级 | ISO 2039-2 | 111 |
| R级 | ASTM D785 | 111 |
| Mechanical properties | Test Condition | Test Method | LOTTE KOREA/Infino TK-2050HL |
|---|---|---|---|
| Tensile modulus | ISO 527-2/5 | 4100 MPa | |
| tensile strength | 屈服 | ISO 527-2/5 | 56.0 MPa |
| elongation | 断裂 | ASTM D638 | 2.1 % |
| tensile strength | 断裂 | ISO 527-2/5 | 56.0 MPa |
| Tensile modulus | ASTM D638 | 4060 MPa | |
| tensile strength | 断裂 | ASTM D638 | 58.8 MPa |
| Flexural modulus | ASTM D790 | 6080 MPa | |
| Tensile strain | 断裂 | ISO 527-2/5 | 2.1 % |
| tensile strength | 屈服 | ASTM D638 | 58.8 MPa |
| bending strength | ASTM D790 | 90.2 MPa | |
| Flexural modulus | ISO 178 | 5200 MPa | |
| bending strength | ISO 178 | 80.0 MPa |
| flammability | Test Condition | Test Method | LOTTE KOREA/Infino TK-2050HL |
|---|---|---|---|
| UL flame retardant rating | 1.530mm | UL 94 | HB |
| physical property | Test Condition | Test Method | LOTTE KOREA/Infino TK-2050HL |
|---|---|---|---|
| melt mass-flow rate | 300°C/2.16kg | ASTM D1238 | 15 g/10min |
| 300°C/2.16kg | ISO 1133 | 15 g/10min | |
| ash content | -- | ASTM D5630 | 51 % |
| Shrinkage rate | MD：3.20mm | ASTM D955 | 0.54 % |
| TD:3.20mm | ISO 2577 | 0.56 % | |
| ash content | -- | ISO 3451 | 51 % |
| Shrinkage rate | TD：3.20mm | ASTM D955 | 0.56 % |
| density | ASTM D792 | 1.77 g/cm³ | |
| ISO 1183 | 1.77 g/cm³ | ||
| Shrinkage rate | MD:3.20mm | ISO 2577 | 0.54 % |
| Thermal performance | Test Condition | Test Method | LOTTE KOREA/Infino TK-2050HL |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,Unannealed,4.00mm，HDT | ISO 75-2/A | 202 °C |
| 1.8MPa,未退火,6.40mm，HDT | ASTM D648 | 202 °C | |
| 0.45MPa,Unannealed,4.00mm，HDT | ISO 75-2/B | 250 °C | |
| 0.45MPa,未退火,6.40mm，HDT | ASTM D648 | 250 °C |