Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D-792 | 2.1-2.15 g/cm |
| Basic performance | Test Condition | Test Method | Test Result |
|---|
| melt mass-flow rate | | ASTM D-1238 | 4-8 g/10min |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Hardness (Shore) | | ASTM D-2240 | 55-60 |
| Tensile modulus | | ASTM D-1708 | 400-500 MPa |
| tensile strength | | ASTM D-1708 | >28 MPa |
| elongation at break | | ASTM D-1708 | >300 % |
| Charpy Notched Impact Strength | | ASTM D-3307 | No Break |
| Other performance | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | V-0 |
| Limiting Oxygen Index | | ASTM D-1003 | 95 % |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| dielectric constant | | ASTM D-150 | 2 |
| Dissipation Factor | | ASTM D-150 | 0.0005 |
| Dissipation Factor | | ASTM D-150 | 0.0005 |
| Surface Resistivity | | ASTM D-257 | >1E+17 ohms |
| Volume resistivity | | ASTM D-257 | >1E+17 ohm·cm |
| dielectric strength | | ASTM D-149 | 35-40 kV/mm |
| dielectric constant | | ASTM D-150 | 2 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| melting temperature | | ASTM D-3307 | 265-275 ℃ |
| Crystallization peak temperature | | ASTM D-3418 | 255-265 ℃ |
| Linear coefficient of thermal expansion - Flow | | ASTM D-696 | 0.00012-0.0002 cm/cm/℃ |
| specific heat | | DSC | 900-1100 J/kg/℃ |
| Crystallization peak temperature | | | 16-24 J/g |
| heat of fusion | | | 16-24 J/g |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.