Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PFA MFA F1530X 美国苏威
--
--
阻燃,高开裂（应力裂纹抗拒）,低流量
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Other performance | Test Condition | Test Method | 美国苏威/MFA F1530X |
|---|---|---|---|
| UL flame retardant rating | UL 94 | V-0 | |
| Limiting Oxygen Index | ASTM D-1003 | 95 % |
| Basic performance | Test Condition | Test Method | 美国苏威/MFA F1530X |
|---|---|---|---|
| melt mass-flow rate | 372℃/5.0kg | ASTM D-1238 | 4-8 g/10min |
| Electrical performance | Test Condition | Test Method | 美国苏威/MFA F1530X |
|---|---|---|---|
| dielectric constant | 23℃，100000Hz | ASTM D-150 | 2 |
| Dissipation Factor | 23℃，100000Hz | ASTM D-150 | 0.0005 |
| 23℃，50Hz | ASTM D-150 | 0.0005 | |
| dielectric strength | 1mm | ASTM D-149 | 35-40 kV/mm |
| Volume resistivity | ASTM D-257 | >1E+17 ohm·cm | |
| dielectric constant | 23℃，50Hz | ASTM D-150 | 2 |
| Surface Resistivity | ASTM D-257 | >1E+17 ohms |
| Mechanical properties | Test Condition | Test Method | 美国苏威/MFA F1530X |
|---|---|---|---|
| tensile strength | 23℃，断裂 | ASTM D-1708 | >28 MPa |
| elongation at break | 23℃ | ASTM D-1708 | >300 % |
| Tensile modulus | 23℃ | ASTM D-1708 | 400-500 MPa |
| Charpy Notched Impact Strength | ASTM D-3307 | No Break | |
| Hardness (Shore) | Shore D | ASTM D-2240 | 55-60 |
| physical property | Test Condition | Test Method | 美国苏威/MFA F1530X |
|---|---|---|---|
| density | ASTM D-792 | 2.1-2.15 g/cm |
| Thermal performance | Test Condition | Test Method | 美国苏威/MFA F1530X |
|---|---|---|---|
| melting temperature | ASTM D-3307 | 265-275 ℃ | |
| specific heat | 23℃ | DSC | 900-1100 J/kg/℃ |
| Linear coefficient of thermal expansion - Flow | Flow | ASTM D-696 | 0.00012-0.0002 cm/cm/℃ |
| Crystallization peak temperature | ASTM D-3418 | 255-265 ℃ | |
| DSC | 16-24 J/g | ||
| heat of fusion | DSC | 16-24 J/g |