PP Fibrolon® P 8540 FKuR Kunststoff GmbH

Properties:
Filler wood fiber 40% filler by weight
Compare

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	11 kJ/m²
Charpy Notched Impact Strength	23°C	ISO 179/1eA	3.6 kJ/m²
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	11 kJ/m²
Charpy Notched Impact Strength	23°C	ISO 179/1eA	3.6 kJ/m²

mechanical properties	Test Condition	Test Method	Test Result
Bending modulus		ISO 178	3500 MPa
Fracture bending strain		ISO 178	6.0 %
Tensile strain change rate		ISO 527	3.0 %
bending strength	3.5%Strain	ISO 178	41.0 MPa
Fracture bending strain		ISO 178	6.0 %
Tensile strain change rate		ISO 527	3.0 %
bending strength	3.5%Strain	ISO 178	41.0 MPa
Tensile strain	Break	ISO 527-2	4.5 %
tensile strength	Break	ISO 527-2	24.0 MPa
tensile strength	tensile strength	Yield	ISO 527-2	26.0 MPa
Tensile modulus		ISO 527-2	3400 MPa
Bending modulus		ISO 178	3500 MPa
Tensile strain	Break	ISO 527-2	4.5 %
tensile strength	Break	ISO 527-2	24.0 MPa
tensile strength	tensile strength	Yield	ISO 527-2	26.0 MPa
Tensile modulus		ISO 527-2	3400 MPa

thermal performance	Test Method	Test Result
Melting temperature	ISO 3146	160to180 °C
Vicat softening temperature	ISO 306/A	155 °C
Melting temperature	ISO 3146	160to180 °C
Vicat softening temperature	ISO 306/A	155 °C

Physical properties	Test Condition	Test Method	Test Result
density		ISO 1183	1.05 g/cm³
Apparent density		ISO 60	0.36 g/cm³
melt mass-flow rate	190°C/5.0kg	ISO 1133	2.0to3.0 g/10min
Melt Volume Flow Rate (MVR)	190°C/5.0kg	ISO 1133	3.00to4.00 cm³/10min
Melt Volume Flow Rate (MVR)	Melt Volume Flow Rate (MVR)	190°C/5.0kg	ISO 1133	3.00to4.00 cm³/10min
density		ISO 1183	1.05 g/cm³
Apparent density		ISO 60	0.36 g/cm³
melt mass-flow rate	190°C/5.0kg	ISO 1133	2.0to3.0 g/10min

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.