ABS 138
0
CompareTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ASTM D-792 | 1.06 g/cm3 | |
| Shrinkage rate | ASTM D-955 | 0.40-0.60 % |
| Basic performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melt mass-flow rate | ASTM D-1238 | 6.0 g/10min |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | ASTM D-638 | 2650 MPa | |
| tensile strength | ASTM D-638 | 46.2 MPa | |
| Flexural modulus | ASTM D-790 | 2690 MPa | |
| bending strength | ASTM D-790 | 75.2 MPa | |
| Impact strength of cantilever beam gap | ASTM D-256 | 48.0 J/m | |
| ASTM D-256 | 165 J/m | ||
| Rockwell hardness | ASTM D-785 | 112 R scale |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat distortion temperature | ASTM D-648 | 93.3 ℃ | |
| ASTM D-648 | 100 ℃ | ||
| ASTM D-648 | 78.9 ℃ | ||
| ASTM D-648 | 96.7 ℃ | ||
| vicat | ASTM D-1525 | 107 ℃ | |
| Linear coefficient of thermal expansion | ASTM D-696 | 0.000081 cm/cm℃ | |
| combustibility | UL 94 | HB | |
| UL 94 | HB |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.