TPEE 655A BK CELANESE SHANGHAI

Form：Granules

Properties:

No fillModerate rigidity

Supplier(0)

Product Description

Certificates(0)

Datasheet

Product Description

Properties:

No fill | Moderate rigidity

Certificates

No Data...

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	NoBreak
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	NoBreak
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	1.5mm	UL 94	HB
elastomer	Test Condition	Test Method	Test Result	Test Unit
tear strength		ASTM D624	212	kN/m
tear strength	tear strength	Flow	ISO 34-1	120	kN/m
Permanent compression deformation	23°C	ASTM D395	<1.0	%
Shore hardness	--	Internal Method	48	%
Shore hardness	Shore hardness	--	ASTM D2632	48	%
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Tensile modulus		ISO 527-2/1A/1	175	Mpa
tensile strength	Yield	ISO 527-2/1A/50	15.0	Mpa
	tensile strength	Break,23°C	ASTM D638	25.2	Mpa
		tensile strength	Break	ISO 527-2/1A/50	30.0	Mpa
			tensile strength	5.0%Strain	ISO 527-2	8.00	Mpa
				tensile strength	10%Strain	ISO 527-2	12.0	Mpa
				tensile strength	tensile strength	50%Strain	ISO 527-2/1A/50	15.0	Mpa
Tensile strain	Yield	ISO 527-2/1A/50	28	%
elongation	Break,23°C	ASTM D638	430	%
Tensile strain	Break	ISO 527-2/1A/50	>300	%
Tensile modulus	23°C	ASTM D638	241	Mpa
Bending modulus	-40°C	ISO 178	700	Mpa
	Bending modulus	23°C	ISO 178	175	Mpa
	Bending modulus	Bending modulus	100°C	ISO 178	86.0	Mpa
bending strength	3.5%Strain	ISO 178	7.00	Mpa
bending strength	bending strength	23°C	ISO 178	10.0	Mpa
RossFlex		Internal Method	>1.0E+6	cycles
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	75.0	°C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	48.0	°C
Glass transition temperature		ASTM D3418	-56.7	°C
Vicat softening temperature		ASTM D1525	181	°C
Melting temperature		ASTM D3418	200	°C
Melting temperature	Melting temperature		ISO 11357-3	200	°C
Linear coefficient of thermal expansion	MD	ISO 11359-2	2E-04	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD	ISO 11359-2	1.7E-04	cm/cm/°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Specific volume		ASTM D792	0.842	cm³/g
melt mass-flow rate		ASTM D1238	7.0to11	g/10min
melt mass-flow rate	melt mass-flow rate	220°C/2.16kg	ISO 1133	10	g/10min
Shrinkage rate	MD	ASTM D955	1.5	%
	Shrinkage rate	TD	ISO 294-4	1.7-2.1	%
	Shrinkage rate	Shrinkage rate	MD	ISO 294-4	1.6-1.9	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Surface resistivity		IEC 60093	4E+15	ohms
Volume resistivity		ASTM D257	5E+12	ohms·cm
Volume resistivity	Volume resistivity		IEC 60093	4E+12	ohms·cm
Dielectric strength		ASTM D149	14	KV/mm
Dielectric strength	Dielectric strength		IEC 60243-1	14	KV/mm
Relative permittivity	1MHz	IEC 60250	4.40
Dissipation factor	1MHz	IEC 60250	0.040
Compared to the anti leakage trace index		ASTM D3638	PLC 0
Compared to the anti leakage trace index	Compared to the anti leakage trace index		IEC 60112	PLC 0
hardness	Test Condition	Test Method	Test Result	Test Unit
Shore hardness	ShoreD	ASTM D2240	55
Shore hardness	Shore hardness	ShoreD,15Sec	ISO 868	55
Supplementary Information	Test Condition	Test Method	Test Result	Test Unit
tear strength		Kg/m	217.2	kN/m

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.