TPEE 655A BK CELANESE SHANGHAI
--
--
No fill、Moderate rigidity
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | CELANESE SHANGHAI/655A BK |
|---|---|---|---|
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | NoBreak |
| 23°C | ISO 179/1eU | NoBreak |
| Supplementary Information | Test Condition | Test Method | CELANESE SHANGHAI/655A BK |
|---|---|---|---|
| tear strength | Kg/m | 217.2 kN/m |
| hardness | Test Condition | Test Method | CELANESE SHANGHAI/655A BK |
|---|---|---|---|
| Shore hardness | 邵氏D | ASTM D2240 | 55 |
| 邵氏D,15秒 | ISO 868 | 55 |
| Mechanical properties | Test Condition | Test Method | CELANESE SHANGHAI/655A BK |
|---|---|---|---|
| Tensile strain | 断裂 | ISO 527-2/1A/50 | >300 % |
| Tensile modulus | ISO 527-2/1A/1 | 175 Mpa | |
| bending strength | 3.5%Strain | ISO 178 | 7.00 Mpa |
| tensile strength | 10%应变 | ISO 527-2 | 12.0 Mpa |
| Flexural modulus | 100°C | ISO 178 | 86.0 Mpa |
| Tensile modulus | 23°C | ASTM D638 | 241 Mpa |
| tensile strength | 断裂,23°C | ASTM D638 | 25.2 Mpa |
| 50%应变 | ISO 527-2/1A/50 | 15.0 Mpa | |
| 断裂 | ISO 527-2/1A/50 | 30.0 Mpa | |
| Tensile strain | 屈服 | ISO 527-2/1A/50 | 28 % |
| RossFlex | 内部方法 | >1.0E+6 cycles | |
| bending strength | 23°C | ISO 178 | 10.0 Mpa |
| Flexural modulus | -40°C | ISO 178 | 700 Mpa |
| 23°C | ISO 178 | 175 Mpa | |
| tensile strength | 屈服 | ISO 527-2/1A/50 | 15.0 Mpa |
| 5.0%应变 | ISO 527-2 | 8.00 Mpa | |
| elongation | 断裂,23°C | ASTM D638 | 430 % |
| Electrical performance | Test Condition | Test Method | CELANESE SHANGHAI/655A BK |
|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 0 | |
| Volume resistivity | ASTM D257 | 5E+12 ohms·cm | |
| dielectric strength | IEC 60243-1 | 14 KV/mm | |
| Volume resistivity | IEC 60093 | 4E+12 ohms·cm | |
| Compared to the Leakage Tracking Index (CTI) | ASTM D3638 | PLC 0 | |
| dielectric strength | ASTM D149 | 14 KV/mm | |
| relative permittivity | 1MHz | IEC 60250 | 4.40 |
| Surface Resistivity | IEC 60093 | 4E+15 ohms | |
| Dissipation Factor | 1MHz | IEC 60250 | 0.040 |
| flammability | Test Condition | Test Method | CELANESE SHANGHAI/655A BK |
|---|---|---|---|
| UL flame retardant rating | 1.5mm | UL 94 | HB |
| physical property | Test Condition | Test Method | CELANESE SHANGHAI/655A BK |
|---|---|---|---|
| Shrinkage rate | MD | ASTM D955 | 1.5 % |
| TD | ISO 294-4 | 1.7-2.1 % | |
| MD | ISO 294-4 | 1.6-1.9 % | |
| melt mass-flow rate | 220°C/2.16kg | ISO 1133 | 10 g/10min |
| Specific volume | ASTM D792 | 0.842 cm³/g | |
| melt mass-flow rate | ASTM D1238 | 7.0to11 g/10min |
| elastomer | Test Condition | Test Method | CELANESE SHANGHAI/655A BK |
|---|---|---|---|
| Shore hardness | -- | 内部方法 | 48 % |
| -- | ASTM D2632 | 48 % | |
| tear strength | 流动方向 | ISO 34-1 | 120 kN/m |
| compression set | 23°C | ASTM D395 | <1.0 % |
| tear strength | ASTM D624 | 212 kN/m |
| Thermal performance | Test Condition | Test Method | CELANESE SHANGHAI/655A BK |
|---|---|---|---|
| vicat | ASTM D1525 | 181 °C | |
| melting temperature | ISO 11357-3 | 200 °C | |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 75.0 °C |
| 1.8MPa,未退火，HDT | ISO 75-2/A | 48.0 °C | |
| melting temperature | ASTM D3418 | 200 °C | |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 2E-04 cm/cm/°C |
| Glass Transition Temperature | ASTM D3418 | -56.7 °C | |
| Linear coefficient of thermal expansion | TD | ISO 11359-2 | 1.7E-04 cm/cm/°C |