PA6 Tarnamid® T-27 Grupa Azoty ATT Polymers GmbH

Usages:
Monofilament
composite
fiber
Compare

Technical Data Sheet

physical property	Test Condition	Test Method	Test Result
density		ISO 1183	1.14 g/cm³
Shrinkage rate		ISO 294-4	0.014 %
Shrinkage rate	Shrinkage rate		ISO 294-4	0.014 %
Water absorption rate		ISO 62	1.8 %
melt mass-flow rate		ISO 1133	120 cm³/10min

Mechanical properties	Test Method	Test Result
Charpy Notched Impact Strength	ISO 179/1eA	5 kJ/m²
Impact strength of simply supported beam without notch	ISO 179/1eU	NB kJ/m²
tensile strength	ISO 527-2	78 MPa
elongation at break	ISO 527-2	50 %
bending strength	ISO 178	82 MPa

Flame retardant performance	Test Condition	Test Method	Test Result
UL flame retardant rating		UL -94	V-2 1.6mm

Electrical performance	Test Condition	Test Method	Test Result
Dissipation Factor		IEC 60112	600 V
	Dissipation Factor		IEC 60093	1E+12 Ω.cm
	Dissipation Factor	Dissipation Factor		IEC 60093	1E+13 Ω.cm
Volume resistivity		IEC 60093	1E+15 Ω.cm
Surface Resistivity		IEC 60093	1E+15 Ω.cm
dielectric strength		IEC 60243-1	30 KV/mm

Thermal performance	Test Condition	Test Method	Test Result
Heat distortion temperature		ISO 75-2/A	60 °C
vicat		ISO 306/A50	195 °C
	vicat	Melting Temperature	ISO 11357-3	221 °C
		vicat		ISO 75	50 °C
		vicat	vicat		PN-EN-60695-2-12	750 °C

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.