Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA6 Tarnamid® T-27 Grupa Azoty ATT Polymers GmbH
--
Monofilament, composite, fiber
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Electrical performance | Test Condition | Test Method | Grupa Azoty ATT Polymers GmbH/Tarnamid® T-27 |
|---|---|---|---|
| Dissipation Factor | 相对漏电起痕指数 | IEC 60112 | 600 V |
| dielectric strength | IEC 60243-1 | 30 KV/mm | |
| Dissipation Factor | 表面电阻 | IEC 60093 | 1E+13 Ω.cm |
| 体积电阻 | IEC 60093 | 1E+12 Ω.cm | |
| Surface Resistivity | IEC 60093 | 1E+15 Ω.cm | |
| Volume resistivity | IEC 60093 | 1E+15 Ω.cm |
| Mechanical properties | Test Condition | Test Method | Grupa Azoty ATT Polymers GmbH/Tarnamid® T-27 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 5 kJ/m² |
| elongation at break | 23°C | ISO 527-2 | 50 % |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | NB kJ/m² |
| tensile strength | 屈服，23°C | ISO 527-2 | 78 MPa |
| bending strength | 23°C | ISO 178 | 82 MPa |
| Flame retardant performance | Test Condition | Test Method | Grupa Azoty ATT Polymers GmbH/Tarnamid® T-27 |
|---|---|---|---|
| UL flame retardant rating | UL -94 | V-2 1.6mm |
| physical property | Test Condition | Test Method | Grupa Azoty ATT Polymers GmbH/Tarnamid® T-27 |
|---|---|---|---|
| Water absorption rate | (23°C,24hr) | ISO 62 | 1.8 % |
| Shrinkage rate | TD | ISO 294-4 | 0.014 % |
| MD | ISO 294-4 | 0.014 % | |
| density | ISO 1183 | 1.14 g/cm³ | |
| melt mass-flow rate | 275℃/5Kg | ISO 1133 | 120 cm³/10min |
| Thermal performance | Test Condition | Test Method | Grupa Azoty ATT Polymers GmbH/Tarnamid® T-27 |
|---|---|---|---|
| vicat | 5.1kg | ISO 306/A50 | 195 °C |
| 热变形温度 | ISO 75 | 50 °C | |
| 灼热丝试验 | PN-EN-60695-2-12 | 750 °C | |
| Heat distortion temperature | 1.80MPa退火，HDT | ISO 75-2/A | 60 °C |
| vicat | 熔融温度 | ISO 11357-3 | 221 °C |