PPO(PPE)+PS+PP

PPO(PPE)+PS+PP NORYL PPX™ PPX640F resin SABIC

Properties:
Filler glass fiber reinforced material 40% filler by weight
Compare

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Impact strength of cantilever beam gap	-30°C	ASTM D256	96 J/m
Dart impact	23°C,TotalEnergy	ASTM D3763	16.8 J
Dart impact	Dart impact	-30°C,TotalEnergy	ASTM D3763	14.1 J
Impact strength of cantilever beam gap	23°C	ASTM D4812	580 J/m
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ASTM D256	110 J/m

mechanical properties	Test Condition	Test Method	Test Result
bending strength	Break,50.0mmSpan	ASTM D790	151 MPa
Bending modulus	50.0mmSpan	ASTM D790	8320 MPa
elongation	Break	ASTM D638	6.4 %
tensile strength	Break	ASTM D638	95.8 MPa
tensile strength	tensile strength	Yield	ASTM D638	95.8 MPa

thermal performance	Test Condition	Test Method	Test Result
Linear coefficient of thermal expansion	MD：-40to40°C	ASTME831	1.1E-05 cm/cm/°C
Vicat softening temperature		ASTM D15254	163 °C
Hot deformation temperature	1.8MPa,Unannealed,3.20mm	ASTM D648	146 °C
Hot deformation temperature	Hot deformation temperature	0.45MPa,Unannealed,3.20mm	ASTM D648	159 °C
Linear coefficient of thermal expansion	TD：-40to40°C	ASTME831	6.3E-05 cm/cm/°C

Physical properties	Test Condition	Test Method	Test Result
Shrinkage rate	TD：3.20mm	Internal Method	0.27to0.61 %
Shrinkage rate	Shrinkage rate	MD：3.20mm	Internal Method	0.17to0.18 %
melt mass-flow rate	260°C/5.0kg	ASTM D1238	1.3 g/10min
density		ASTM D792	1.30 g/cm³

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.