PPO(PPE)+PS+PP NORYL PPX™ PPX640F resin SABIC
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC/NORYL PPX™ PPX640F resin |
|---|---|---|---|
| Impact strength of cantilever beam gap | 23°C | ASTM D256 | 110 J/m |
| Dart impact | 23°C,TotalEnergy | ASTM D3763 | 16.8 J |
| Impact strength of cantilever beam gap | -30°C | ASTM D256 | 96 J/m |
| Dart impact | -30°C,TotalEnergy | ASTM D3763 | 14.1 J |
| Impact strength of cantilever beam gap | 23°C | ASTM D4812 | 580 J/m |
| Mechanical properties | Test Condition | Test Method | SABIC/NORYL PPX™ PPX640F resin |
|---|---|---|---|
| elongation | 断裂 | ASTM D638 | 6.4 % |
| bending strength | Break,50.0mmSpan | ASTM D790 | 151 MPa |
| tensile strength | 断裂 | ASTM D638 | 95.8 MPa |
| 屈服 | ASTM D638 | 95.8 MPa | |
| Flexural modulus | 50.0mm跨距 | ASTM D790 | 8320 MPa |
| physical property | Test Condition | Test Method | SABIC/NORYL PPX™ PPX640F resin |
|---|---|---|---|
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.17to0.18 % |
| melt mass-flow rate | 260°C/5.0kg | ASTM D1238 | 1.3 g/10min |
| Shrinkage rate | TD：3.20mm | 内部方法 | 0.27to0.61 % |
| density | ASTM D792 | 1.30 g/cm³ |
| Thermal performance | Test Condition | Test Method | SABIC/NORYL PPX™ PPX640F resin |
|---|---|---|---|
| Linear coefficient of thermal expansion | TD：-40到40°C | ASTME831 | 6.3E-05 cm/cm/°C |
| vicat | ASTM D15254 | 163 °C | |
| Heat distortion temperature | 0.45MPa,未退火,3.20mm，HDT | ASTM D648 | 159 °C |
| Linear coefficient of thermal expansion | MD：-40到40°C | ASTME831 | 1.1E-05 cm/cm/°C |
| Heat distortion temperature | 1.8MPa,未退火,3.20mm，HDT | ASTM D648 | 146 °C |