Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Melt volume flow rate | | ISO 1133 | 11.0 cm3/10min |
| Water absorption rate | | ISO 62 | 1.6 % |
| Water absorption rate | | ASTM D570 | 1.1 % |
| Shore hardness | | ASTM D785 | 78 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| Flammability level | | UL 94 | HB |
| Flammability level | | UL 94 | HB |
| Limiting Oxygen Index | | ISO 4589-2 | 22 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO 527-2 | 405 Mpa |
| tensile strength | | ISO 527-2 | 27.0 Mpa |
| Tensile strain | | ISO 527-2 | 42 % |
| Nominal tensile fracture strain | | ISO 527-2 | > 50 % |
| Fracture tensile strength | | ASTM D638 | 64.1 Mpa |
| elongation | | ASTM D638 | 430 % |
| Flexural modulus | | ASTM D790 | 338 Mpa |
| Impact strength of cantilever beam gap | | ASTM D256 | 320 J/m |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of simply supported beam without notch | | ISO 179/1eU | -- |
| Impact strength of simply supported beam without notch | | ISO 179/1eU | -- |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | IEC 60093 | -- ohms |
| Volume resistivity | | IEC 60093 | -- ohms·cm |
| dielectric strength | | IEC 60243-1 | -- KV/mm |
| relative permittivity | | IEC 60250 | 10.0 |
| relative permittivity | | IEC 60250 | 4.00 |
| Dissipation Factor | | IEC 60250 | 0.18 |
| Dissipation Factor | | IEC 60250 | 0.096 |
| Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | V |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ISO 75-2/B | 130 °C |
| Heat distortion temperature | | ISO 75-2/A | 45.0 °C |
| vicat | | ISO 306/B50 | 140 °C |
| melting temperature | | ISO 11357-3 | 182 °C |
| Linear coefficient of thermal expansion | | ISO 11359-2 | 1.1E-4 cm/cm/°C |
| melting temperature | | DSC | 186 °C |
| Heat distortion temperature | | QJ/CL.4.3.19 | 41.1 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.