Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Shrinkage rate | | ISO 294-4 | 0.95-1.3 % |
| Shrinkage rate | | ISO 294-4 | 0.50-0.70 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | HB |
| UL flame retardant rating | | UL 94 | HB |
| UL flame retardant rating | | UL 94 | HB |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| dimensional stability | | | 46.0 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| coefficient of friction | | ASTM D1894 | 0.30 |
| Wear factor | | ASTM D3702 | 6E-07 mm³/Nm |
| Tensile modulus | | ISO 527-2/1 | 6300 Mpa |
| tensile strength | | ISO 527-2/5 | 120 Mpa |
| Tensile strain | | ISO 527-2/5 | 2.5 % |
| coefficient of friction | | ASTM D1894 | 0.22 |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of simply supported beam without notch | | ISO 179/1eU | 40 kJ/m² |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ISO 75-2/B | 265 °C |
| Heat distortion temperature | | ISO 75-2/A | 250 °C |
| vicat | | ISO 306/B50 | 250 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.