PA66 66-20T G/20 LATI ITALY
LATAMID
--
Filler: Glass fiber reinf、20% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | LATI ITALY/66-20T G/20 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 40 kJ/m² |
| Supplementary Information | Test Condition | Test Method | LATI ITALY/66-20T G/20 |
|---|---|---|---|
| dimensional stability | 46.0 |
| Mechanical properties | Test Condition | Test Method | LATI ITALY/66-20T G/20 |
|---|---|---|---|
| Tensile strain | 断裂,23°C | ISO 527-2/5 | 2.5 % |
| tensile strength | 断裂,23°C | ISO 527-2/5 | 120 Mpa |
| coefficient of friction | Dynamic | ASTM D1894 | 0.22 |
| Wear factor | ASTM D3702 | 6E-07 mm³/Nm | |
| Tensile modulus | 23°C | ISO 527-2/1 | 6300 Mpa |
| coefficient of friction | Static | ASTM D1894 | 0.30 |
| flammability | Test Condition | Test Method | LATI ITALY/66-20T G/20 |
|---|---|---|---|
| UL flame retardant rating | 0.75mm | UL 94 | HB |
| 3.0mm | UL 94 | HB | |
| 1.5mm | UL 94 | HB |
| physical property | Test Condition | Test Method | LATI ITALY/66-20T G/20 |
|---|---|---|---|
| Shrinkage rate | MD:2.00mm | ISO 294-4 | 0.50-0.70 % |
| TD:2.00mm | ISO 294-4 | 0.95-1.3 % |
| Thermal performance | Test Condition | Test Method | LATI ITALY/66-20T G/20 |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 265 °C |
| vicat | ISO 306/B50 | 250 °C | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 250 °C |