Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| melt mass-flow rate | | ASTM D1238 | 17 g/10 min |
| melt mass-flow rate | | ASTM D1238 | 23 g/10 min |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | ASTM D785 | 100 |
| Rockwell hardness | | ISO 2039-2 | 100 |
| Rockwell hardness | | ASTM D785 | 94 |
| Rockwell hardness | | ISO 2039-2 | 94 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | HB |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | | ASTM D638 | 42.0 Mpa |
| Flexural modulus | | ASTM D790 | 2550 Mpa |
| bending strength | | ASTM D790 | 72.0 Mpa |
| tensile strength | | ASTM D638 | 39.0 Mpa |
| Flexural modulus | | ASTM D790 | 2160 Mpa |
| bending strength | | ASTM D790 | 67.0 Mpa |
| injection | Test Condition | Test Method | Test Result |
|---|
| Processing (melt) temperature | | | 190 to 230 °C |
| Injection Pressure | | | 68.6 to 108 Mpa |
| drying temperature | | | 80 to 85 °C |
| drying time | | | 2.0 to 3.0 hr |
| Processing (melt) temperature | | | 180 to 220 °C |
| Temperature | | | 40 to 80 °C |
| Injection Pressure | | | 58.8 to 108 Mpa |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Hot deformation temperature (HDT) | | ASTM D648 | 83.0 °C |
| vicat | | ASTM D746 | 95.0 °C |
| Hot deformation temperature (HDT) | | ASTM D648 | 82.0 °C |
| vicat | | ASTM D746 | 94.0 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.