Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
ASA WG1800 FCFC TAIWAN
TAIRILAC®
Outdoor applications
Weather resistance
TDS
Processing
MSDS
UL
SVHC
PSC
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| hardness | Test Condition | Test Method | FCFC TAIWAN/WG1800 |
|---|---|---|---|
| Rockwell hardness | R 计秤, 23°C | ISO 2039-2 | 94 |
| R 级, 23°C | ASTM D785 | 94 |
| Mechanical properties | Test Condition | Test Method | FCFC TAIWAN/WG1800 |
|---|---|---|---|
| bending strength | 23°C | ASTM D790 | 67.0 Mpa |
| Flexural modulus | 23°C | ASTM D790 | 2160 Mpa |
| tensile strength | 23°C | ASTM D638 | 39.0 Mpa |
| flammability | Test Condition | Test Method | FCFC TAIWAN/WG1800 |
|---|---|---|---|
| UL flame retardant rating | 1.5 mm | UL 94 | HB |
| physical property | Test Condition | Test Method | FCFC TAIWAN/WG1800 |
|---|---|---|---|
| melt mass-flow rate | 220°C/10.0 kg | ASTM D1238 | 23 g/10 min |
| Thermal performance | Test Condition | Test Method | FCFC TAIWAN/WG1800 |
|---|---|---|---|
| Heat distortion temperature | 1.8 MPa, 未退火, 6.35 mm，HDT | ASTM D648 | 82.0 °C |
| vicat | ASTM D746 | 94.0 °C |
| injection | Test Condition | Test Method | FCFC TAIWAN/WG1800 |
|---|---|---|---|
| drying time | 2.0 to 3.0 hr | ||
| Injection Pressure | 58.8 to 108 Mpa | ||
| Processing (melt) temperature | 180 to 220 °C | ||
| drying temperature | 80 to 85 °C | ||
| Temperature | 40 to 80 °C |