PC/PET XYLEX™ X7200-NA9A008
168
- Properties:UV resistanceHigh mobility
- Usages:Industrial applicationsElectronic fieldElectrical fieldAutomotive sector
Compare
View PricesTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melt mass-flow rate | ASTM D1238 | 16 g/10min | |
| Melt volume flow rate | ISO 1133 | 18.0 cm3/10min | |
| Shrinkage rate | 内部方法 | 0.60-0.80 % | |
| 内部方法 | 0.60-0.80 % | ||
| Water absorption rate | ISO 62 | 0.050 % | |
| ISO 62 | 0.020 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| tensile strength | ASTM D638 | 33.8 Mpa | |
| ISO 527-2/50 | 34.0 Mpa | ||
| ASTM D638 | 27.6 Mpa | ||
| ISO 527-2/50 | 28.0 Mpa | ||
| elongation | ASTM D638 | 10 % | |
| Tensile strain | ISO 527-2/50 | 8.2 % | |
| elongation | ASTM D638 | 130 % | |
| Tensile strain | ISO 527-2/50 | 120 % | |
| Flexural modulus | ASTM D790 | 1450 Mpa | |
| ISO 178 | 1610 Mpa | ||
| Tensile modulus | ASTM D638 | 1240 Mpa | |
| ISO 527-2/1 | 1670 Mpa | ||
| bending strength | ISO 178 | 48.0 Mpa | |
| ASTM D790 | 49.0 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Suspended wall beam without notch impact strength | ISO 180/1U | NoBreak | |
| ISO 180/1U | NoBreak | ||
| Dart impact | ASTM D3763 | 36.2 J | |
| Charpy Notched Impact Strength | ISO 179/1eA | 6.1 kJ/m² | |
| ISO 179/1eA | 12 kJ/m² | ||
| Impact strength of simply supported beam without notch | ISO 179/1eU | 80 kJ/m² | |
| ISO 179/1eU | NoBreak | ||
| Impact strength of cantilever beam gap | ISO 180/1A | 8.0 kJ/m² | |
| ISO 180/1A | 14 kJ/m² |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Linear coefficient of thermal expansion | ASTME831 | 9.9E-05 cm/cm/°C | |
| ISO 11359-2 | 9.9E-05 cm/cm/°C | ||
| ASTME831 | 1.1E-04 cm/cm/°C | ||
| ISO 11359-2 | 1.1E-04 cm/cm/°C | ||
| Heat distortion temperature | ASTM D648 | 110 °C | |
| ASTM D648 | 71.1 °C | ||
| ISO 75-2/Af | 73.4 °C | ||
| vicat | ASTM D152510 | 146 °C | |
| ISO 306/B50 | 103 °C | ||
| ISO 306/B120 | 107 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.