Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC/PET X7200-NA9A008 SABIC INNOVATIVE US
XYLEX™
Industrial applications、Electronic field、Electrical field、Automotive sector
UV resistance、High mobility
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE US/X7200-NA9A008 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 12 kJ/m² |
| Dart impact | 23°C,TotalEnergy | ASTM D3763 | 36.2 J |
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 6.1 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | NoBreak |
| Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 8.0 kJ/m² |
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | NoBreak |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 14 kJ/m² |
| Suspended wall beam without notch impact strength | -30°C | ISO 180/1U | NoBreak |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 80 kJ/m² |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/X7200-NA9A008 |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1 | 1670 Mpa | |
| elongation | 屈服 | ASTM D638 | 10 % |
| tensile strength | 断裂 | ASTM D638 | 27.6 Mpa |
| Tensile strain | 屈服 | ISO 527-2/50 | 8.2 % |
| tensile strength | 断裂 | ISO 527-2/50 | 28.0 Mpa |
| Flexural modulus | 50.0mm跨距 | ASTM D790 | 1450 Mpa |
| tensile strength | 屈服 | ISO 527-2/50 | 34.0 Mpa |
| Tensile modulus | ASTM D638 | 1240 Mpa | |
| elongation | 断裂 | ASTM D638 | 130 % |
| bending strength | 屈服,50.0mm跨距 | ASTM D790 | 49.0 Mpa |
| ISO 178 | 48.0 Mpa | ||
| Flexural modulus | ISO 178 | 1610 Mpa | |
| tensile strength | 屈服 | ASTM D638 | 33.8 Mpa |
| Tensile strain | 断裂 | ISO 527-2/50 | 120 % |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE US/X7200-NA9A008 |
|---|---|---|---|
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.60-0.80 % |
| melt mass-flow rate | 260°C/5.0kg | ASTM D1238 | 16 g/10min |
| Shrinkage rate | TD：3.20mm | 内部方法 | 0.60-0.80 % |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.020 % |
| 饱和,23°C | ISO 62 | 0.050 % | |
| Melt volume flow rate | 260°C/5.0kg | ISO 1133 | 18.0 cm3/10min |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/X7200-NA9A008 |
|---|---|---|---|
| vicat | -- | ISO 306/B120 | 107 °C |
| Linear coefficient of thermal expansion | TD：-40到40°C | ASTME831 | 1.1E-04 cm/cm/°C |
| TD：-40到40°C | ISO 11359-2 | 1.1E-04 cm/cm/°C | |
| MD：-40到40°C | ASTME831 | 9.9E-05 cm/cm/°C | |
| Heat distortion temperature | 0.45MPa,未退火,3.20mm，HDT | ASTM D648 | 110 °C |
| vicat | -- | ISO 306/B50 | 103 °C |
| Linear coefficient of thermal expansion | MD：-40到40°C | ISO 11359-2 | 9.9E-05 cm/cm/°C |
| Heat distortion temperature | 1.8MPa,Unannealed,64.0mmSpan，HDT | ISO 75-2/Af | 73.4 °C |
| vicat | ASTM D152510 | 146 °C | |
| Heat distortion temperature | 1.8MPa,未退火,3.20mm，HDT | ASTM D648 | 71.1 °C |