Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTMD792 | 1.20 g/cm³ |
| Shrinkage rate | | ASTM D955 | 0.40to0.70 % |
| Shrinkage rate | | ASTM D955 | 0.40to0.70 % |
| Water absorption rate | | ASTMD570 | 0.10 % |
| Water absorption rate | Saturation | ASTM D570 | 0.40 % |
| Water absorption rate | | ISO 62 | 0.40 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | V-0 |
| Hot filament ignition temperature | | IEC 60695-2-13 | 960 °C |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | Yield | ASTMD638 | 50.0 MPa |
| Flexural modulus | | ASTMD790 | 2100 MPa |
| bending strength | | ISO 178 | 70.0 MPa |
| bending strength | Yield | ASTM D790 | 70.0 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO 179 | 20 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO 179 | 无断裂 |
| Impact strength of cantilever beam gap | | ASTMD256 | 500 J/m |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | PLC 3 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ASTMD648 | 110 °C |
| vicat | | ASTMD15255 | 135 °C |
| vicat | | ASTMD15256 | 125 °C |
| ball-indentation hardness | | VDE0470 | 通过 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.