PC+ABS TAROBLEND 85 X0 Taro Plast S.p.A.
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Taro Plast S.p.A./TAROBLEND 85 X0 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179 | 20 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179 | 无断裂 |
| Impact strength of cantilever beam gap | ASTMD256 | 500 J/m |
| Mechanical properties | Test Condition | Test Method | Taro Plast S.p.A./TAROBLEND 85 X0 |
|---|---|---|---|
| Flexural modulus | ASTMD790 | 2100 MPa | |
| bending strength | 屈服 | ASTM D790 | 70.0 MPa |
| tensile strength | 屈服 | ASTMD638 | 50.0 MPa |
| bending strength | --3 | ISO 178 | 70.0 MPa |
| Electrical performance | Test Condition | Test Method | Taro Plast S.p.A./TAROBLEND 85 X0 |
|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | 解决方案A | IEC 60112 | PLC 3 |
| flammability | Test Condition | Test Method | Taro Plast S.p.A./TAROBLEND 85 X0 |
|---|---|---|---|
| Hot filament ignition temperature | IEC 60695-2-13 | 960 °C | |
| UL flame retardant rating | 1.7mm | UL 94 | V-0 |
| physical property | Test Condition | Test Method | Taro Plast S.p.A./TAROBLEND 85 X0 |
|---|---|---|---|
| Shrinkage rate | MD | ASTM D955 | 0.40to0.70 % |
| Water absorption rate | 饱和 | ASTM D570 | 0.40 % |
| density | ASTMD792 | 1.20 g/cm³ | |
| Water absorption rate | 23°C,24hr | ASTMD570 | 0.10 % |
| 饱和,23°C | ISO 62 | 0.40 % | |
| Shrinkage rate | TD | ASTM D955 | 0.40to0.70 % |
| Thermal performance | Test Condition | Test Method | Taro Plast S.p.A./TAROBLEND 85 X0 |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTMD648 | 110 °C |
| ball-indentation hardness | 125°C | VDE0470 | 通过 |
| vicat | -- | ASTMD15255 | 135 °C |
| -- | ASTMD15256 | 125 °C |