PC/PET XYLEX™ X7300
110
- Properties:UV resistanceHigh mobility
- Usages:Automotive sector
Compare
View PricesTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melt mass-flow rate | ASTMD1238 | 21 g/10min | |
| Melt volume flow rate | ISO1133 | 21.0 cm3/10min | |
| Shrinkage rate | 内部方法 | 0.40to0.80 % | |
| 内部方法 | 0.50to0.70 % |
| optical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| transmissivity | ASTMD1003 | 88.0 % | |
| Haze ratio | ASTMD1003 | 2.0 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | ASTMD638 | 1840 Mpa | |
| ISO527-2/1 | 1900 Mpa | ||
| tensile strength | ASTMD638 | 49.0 Mpa | |
| Tensile stress | ISO527-2/50 | 55.0 Mpa | |
| tensile strength | ASTMD638 | 52.0 Mpa | |
| Tensile stress | ISO527-2/50 | 55.0 Mpa | |
| elongation | ASTMD638 | 5.0 % | |
| Tensile strain | ISO527-2/50 | 5.0 % | |
| elongation | ASTMD638 | 150 % | |
| Tensile strain | ISO527-2/50 | >150 % | |
| Flexural modulus | ASTMD790 | 1940 Mpa | |
| ISO178 | 2000 Mpa | ||
| Bending strength 5,6 | ISO178 | 71.0 Mpa | |
| bending strength | ASTMD790 | 83.0 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| NotchedIzodImpactStrength7 | ISO180/1A | 9.0 kJ/m² | |
| Dart impact equipped with measuring instruments | ASTMD3763 | 95.0 J |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| ASTME831 | 1.1E-04 cm/cm/°C | ||
| ISO11359-2 | 8.5E-05 cm/cm/°C | ||
| Heat distortion temperature | ASTMD648 | 102 °C | |
| ASTMD648 | 88.0 °C | ||
| ISO75-2/Ae | 90.0 °C | ||
| vicat | ASTMD15259 | 108 °C | |
| ISO306/B120 | 106 °C | ||
| ASTME831 | 1.2E-04 cm/cm/°C | ||
| ISO11359-2 | 8.5E-05 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.