PC/PET X7300 SABIC INNOVATIVE CANADA
XYLEX™
Automotive sector
UV resistance、High mobility
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE CANADA/X7300 |
|---|---|---|---|
| NotchedIzodImpactStrength7 | 23°C | ISO180/1A | 9.0 kJ/m² |
| Dart impact equipped with measuring instruments | 23°C,TotalEnergy | ASTMD3763 | 95.0 J |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE CANADA/X7300 |
|---|---|---|---|
| Tensile stress | 屈服 | ISO527-2/50 | 55.0 Mpa |
| elongation | 断裂 | ASTMD638 | 150 % |
| Bending strength 5,6 | ISO178 | 71.0 Mpa | |
| Tensile modulus | ASTMD638 | 1840 Mpa | |
| Tensile strain | 屈服 | ISO527-2/50 | 5.0 % |
| Tensile stress | 断裂 | ISO527-2/50 | 55.0 Mpa |
| elongation | 屈服 | ASTMD638 | 5.0 % |
| Tensile modulus | ISO527-2/1 | 1900 Mpa | |
| tensile strength | 屈服 | ASTMD638 | 49.0 Mpa |
| bending strength | 屈服,50.0mm跨距 | ASTMD790 | 83.0 Mpa |
| tensile strength | 断裂 | ASTMD638 | 52.0 Mpa |
| Tensile strain | 断裂 | ISO527-2/50 | >150 % |
| Flexural modulus | ISO178 | 2000 Mpa | |
| 50.0mm跨距 | ASTMD790 | 1940 Mpa |
| optical performance | Test Condition | Test Method | SABIC INNOVATIVE CANADA/X7300 |
|---|---|---|---|
| transmissivity | 2540µm | ASTMD1003 | 88.0 % |
| Haze ratio | 2540µm | ASTMD1003 | 2.0 % |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE CANADA/X7300 |
|---|---|---|---|
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.40to0.80 % |
| Melt volume flow rate | 265°C/2.16kg | ISO1133 | 21.0 cm3/10min |
| melt mass-flow rate | 265°C/2.16kg | ASTMD1238 | 21 g/10min |
| Shrinkage rate | TD：3.20mm | 内部方法 | 0.50to0.70 % |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE CANADA/X7300 |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,未退火,3.20mm | ASTMD648 | 102 °C |
| TD：23to60°C | ISO11359-2 | 8.5E-05 cm/cm/°C | |
| 1.8MPa,Unannealed,100mmSpan | ISO75-2/Ae | 90.0 °C | |
| MD：-40到40°C | ASTME831 | 1.2E-04 cm/cm/°C | |
| MD：23到60°C | ISO11359-2 | 8.5E-05 cm/cm/°C | |
| Heat distortion temperature | 1.8MPa,未退火,3.20mm | ASTMD648 | 88.0 °C |
| vicat | ASTMD15259 | 108 °C | |
| ISO306/B120 | 106 °C | ||
| TD：-40到40°C | ASTME831 | 1.1E-04 cm/cm/°C |