Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| flow | | ASTM D955 | 0.20to0.60 % |
| Water absorption rate | | ASTMD570 | 0.10 % |
| density | | ASTMD792 | 1.05 g/cm³ |
| melt mass-flow rate | | ASTM D1238 | 6.0 g/10min |
| Melt volume flow rate | | ISO 1133 | 6.00 cm³/10min |
| Melt volume flow rate | | ISO 1133 | 65.0 cm³/10min |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Hardness (Rockwell R) | | ASTM D785 | 62 |
| Hardness (Rockwell R) | | ISO 2039-2 | 62 |
| ball-indentation hardness | | ISO 2039-1 | 35.0 MPa |
| optical performance | Test Condition | Test Method | Test Result |
|---|
| transmissivity | | ASTM D1003 | 91.0 % |
| Haze ratio | | ASTM D1003 | 2.0 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| yield | | ASTM D638 | 23.4 MPa |
| yield | | ISO 527-2 | 28.0 MPa |
| fracture | | ASTM D638 | 70 % |
| fracture | | ISO 527-2 | 120 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Suspended wall beam without notch impact strength | | ISO 180 | 200 kJ/m² |
| Dart impact | | ASTM D5420 | 19.2 J |
| Charpy Notched Impact Strength | | ISO 179 | 16 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO 179 | 无断裂 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| maximum service temperature | | | 250 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.