Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
MMBS ZYLAR® 960 INEOS Barex
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | INEOS Barex/ZYLAR® 960 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179 | 16 kJ/m² |
| Dart impact | ASTM D5420 | 19.2 J | |
| Impact strength of simply supported beam without notch | 23°C | ISO 179 | 无断裂 |
| Suspended wall beam without notch impact strength | ISO 180 | 200 kJ/m² |
| hardness | Test Condition | Test Method | INEOS Barex/ZYLAR® 960 |
|---|---|---|---|
| Hardness (Rockwell R) | ASTM D785 | 62 | |
| ball-indentation hardness | ISO 2039-1 | 35.0 MPa | |
| Hardness (Rockwell R) | ISO 2039-2 | 62 |
| Mechanical properties | Test Condition | Test Method | INEOS Barex/ZYLAR® 960 |
|---|---|---|---|
| fracture | ASTM D638 | 70 % | |
| ISO 527-2 | 120 % | ||
| yield | ASTM D638 | 23.4 MPa | |
| ISO 527-2 | 28.0 MPa |
| optical performance | Test Condition | Test Method | INEOS Barex/ZYLAR® 960 |
|---|---|---|---|
| transmissivity | 550nm | ASTM D1003 | 91.0 % |
| Haze ratio | ASTM D1003 | 2.0 % |
| physical property | Test Condition | Test Method | INEOS Barex/ZYLAR® 960 |
|---|---|---|---|
| Melt volume flow rate | 220°C/10.0kg | ISO 1133 | 65.0 cm³/10min |
| melt mass-flow rate | 200°C/5.0kg | ASTM D1238 | 6.0 g/10min |
| density | ASTMD792 | 1.05 g/cm³ | |
| flow | ASTM D955 | 0.20to0.60 % | |
| Melt volume flow rate | 200°C/5.0kg | ISO 1133 | 6.00 cm³/10min |
| Water absorption rate | 饱和,23°C | ASTMD570 | 0.10 % |
| Thermal performance | Test Condition | Test Method | INEOS Barex/ZYLAR® 960 |
|---|---|---|---|
| maximum service temperature | 250 °C |