Technical Data Sheet
physical property | Test Condition | Test Method | Test Result |
---|
density | | ASTMD792 | 1.20 g/cm³ |
melt mass-flow rate | | ASTM D1238 | 28 g/10min |
Shrinkage rate | | 内部方法 | 0.23 % |
Shrinkage rate | | 内部方法 | 0.31 % |
Water absorption rate | | ISO 62 | 0.29 % |
flammability | Test Condition | Test Method | Test Result |
---|
UL flame retardant rating | | UL 94 | V-0 |
UL flame retardant rating | | UL 94 | 5VB |
UL flame retardant rating | | UL 94 | V-1 |
Mechanical properties | Test Condition | Test Method | Test Result |
---|
fracture | | 内部方法 | 79 % |
fracture | | ASTM D638 | 99 % |
fracture | | ISO 527-2/50 | 99 % |
yield | | 内部方法 | 59.0 MPa |
yield | | ASTM D638 | 56.0 MPa |
yield | | ISO 527-2/50 | 57.0 MPa |
yield | | ASTM D790 | 89.0 MPa |
Impact resistance | Test Condition | Test Method | Test Result |
---|
Charpy Notched Impact Strength | | ISO 179/1eA | 11 kJ/m² |
Impact strength of cantilever beam gap | | ASTM D256 | 370 J/m |
Electrical performance | Test Condition | Test Method | Test Result |
---|
Surface Resistivity | | ASTM D257 | 1E+15 ohms |
Compared to the Leakage Tracking Index (CTI) | | UL 746 | PLC 0 |
Thermal performance | Test Condition | Test Method | Test Result |
---|
Linear coefficient of thermal expansion | | ASTME831 | 7E-05 cm/cm/°C |
Linear coefficient of thermal expansion | | ASTME831 | 6.7E-05 cm/cm/°C |
RTI Elec | | UL 746 | 60.0 °C |
RTI Imp | | UL 746 | 60.0 °C |
RTI | | UL 746 | 60.0 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.