Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC CY6025 resin SABIC
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC/CY6025 resin |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 11 kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ASTM D256 | 370 J/m |
| Mechanical properties | Test Condition | Test Method | SABIC/CY6025 resin |
|---|---|---|---|
| fracture | ISO 527-2/50 | 99 % | |
| ASTM D638 | 99 % | ||
| yield | ASTM D638 | 56.0 MPa | |
| fracture | 内部方法 | 79 % | |
| yield | 内部方法 | 59.0 MPa | |
| ISO 527-2/50 | 57.0 MPa | ||
| ASTM D790 | 89.0 MPa |
| Electrical performance | Test Condition | Test Method | SABIC/CY6025 resin |
|---|---|---|---|
| Surface Resistivity | ASTM D257 | 1E+15 ohms | |
| Compared to the Leakage Tracking Index (CTI) | CTI | UL 746 | PLC 0 |
| flammability | Test Condition | Test Method | SABIC/CY6025 resin |
|---|---|---|---|
| UL flame retardant rating | 1.00mm | UL 94 | V-1 |
| 1.20mm | UL 94 | V-0 | |
| 1.50mm | UL 94 | 5VB |
| physical property | Test Condition | Test Method | SABIC/CY6025 resin |
|---|---|---|---|
| Shrinkage rate | MD | 内部方法 | 0.23 % |
| melt mass-flow rate | 260°C/2.16kg | ASTM D1238 | 28 g/10min |
| density | ASTMD792 | 1.20 g/cm³ | |
| Water absorption rate | 饱和,23°C | ISO 62 | 0.29 % |
| Shrinkage rate | TD | 内部方法 | 0.31 % |
| Thermal performance | Test Condition | Test Method | SABIC/CY6025 resin |
|---|---|---|---|
| Linear coefficient of thermal expansion | TD:-40到40°C | ASTME831 | 6.7E-05 cm/cm/°C |
| RTI Imp | UL 746 | 60.0 °C | |
| RTI | UL 746 | 60.0 °C | |
| Linear coefficient of thermal expansion | MD:-40到40°C | ASTME831 | 7E-05 cm/cm/°C |
| RTI Elec | UL 746 | 60.0 °C |