Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Chlorine content | | ISO 1158 | 67.0 wt% |
| density | | JISK7112 | 1.56 g/cm³ |
| Apparent density | | JISK6720-2 | 0.50to0.60 g/cm³ |
| K-Value | | JISK6720-2 | 66.0 |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| temperature | | JISK6745 | 93 °C |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | Yield | JISK7113 | 61.0 MPa |
| Tensile strain | Break | JISK7113 | 60 % |
| Flexural modulus | | JISK7171 | 2850 MPa |
| bending strength | | JISK7171 | 89.0 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of simply supported beam without notch | | JISK7111 | 23 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Volume resistivity | | | 1E+15 ohms·cm |
| dielectric strength | | | 47to63 kV/mm |
| dielectric constant | | | 3.08 |
| dielectric constant | | | 3.20to3.60 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | JISK7191-1 | 93.0 °C |
| vicat | | JISK7206 | 116 °C |
| Linear coefficient of thermal expansion | | ASTM D696 | 7.0E-5到7.5E-5 cm/cm/°C |
| Heat loss | | JISK6720-2 | <0.3 wt% |
| Heat distortion temperature | | JISK7207 | 103 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.