Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PVC Sekisui PVC HA-53K Sekisui (Hong Kong) Limited
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Sekisui (Hong Kong) Limited/Sekisui PVC HA-53K |
|---|---|---|---|
| Impact strength of simply supported beam without notch | JISK7111 | 23 kJ/m² |
| Supplementary Information | Test Condition | Test Method | Sekisui (Hong Kong) Limited/Sekisui PVC HA-53K |
|---|---|---|---|
| temperature | 弯曲 (Flex) | JISK6745 | 93 °C |
| Mechanical properties | Test Condition | Test Method | Sekisui (Hong Kong) Limited/Sekisui PVC HA-53K |
|---|---|---|---|
| Flexural modulus | JISK7171 | 2850 MPa | |
| Tensile strain | 断裂 | JISK7113 | 60 % |
| tensile strength | 屈服 | JISK7113 | 61.0 MPa |
| bending strength | JISK7171 | 89.0 MPa |
| Electrical performance | Test Condition | Test Method | Sekisui (Hong Kong) Limited/Sekisui PVC HA-53K |
|---|---|---|---|
| dielectric constant | 60Hz | 3.08 | |
| 1MHz | 3.20to3.60 | ||
| dielectric strength | 47to63 kV/mm | ||
| Volume resistivity | 23°C | 1E+15 ohms·cm |
| physical property | Test Condition | Test Method | Sekisui (Hong Kong) Limited/Sekisui PVC HA-53K |
|---|---|---|---|
| Apparent density | JISK6720-2 | 0.50to0.60 g/cm³ | |
| K-Value | JISK6720-2 | 66.0 | |
| density | JISK7112 | 1.56 g/cm³ | |
| Chlorine content | ISO 1158 | 67.0 wt% |
| Thermal performance | Test Condition | Test Method | Sekisui (Hong Kong) Limited/Sekisui PVC HA-53K |
|---|---|---|---|
| vicat | JISK7206 | 116 °C | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | JISK7191-1 | 93.0 °C |
| 0.45MPa,未退火，HDT | JISK7207 | 103 °C | |
| Linear coefficient of thermal expansion | MD | ASTM D696 | 7.0E-5到7.5E-5 cm/cm/°C |
| Heat loss | JISK6720-2 | <0.3 wt% |