Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO1183 | 1.32到1.36 g/cm³ |
| density | | ISO1183 | 1.40到1.45 g/cm³ |
| Shrinkage rate | | | 0.20到0.30 % |
| Shrinkage rate | | | 0.25到0.35 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| | ISO868 | 75到80 |
| | ISO868 | 80到85 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL94 | V-0 |
| Hot filament ignition temperature | | VDE0471/2 | 960 °C |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO527-2 | 7500到10000 MPa |
| Tensile stress | Yield | ISO527-2 | 170到220 MPa |
| Tensile strain | Break | ISO527-2 | >3.0 % |
| Tensile modulus | | ISO527-2 | 7500到10000 MPa |
| Tensile stress | Yield | ISO527-2 | 120到150 MPa |
| Tensile strain | Break | ISO527-2 | >3.0 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ISO180/1A | >8.0 kJ/m² |
| Impact strength of cantilever beam gap | | ISO180/1A | >10 kJ/m² |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ISO75-2/A | 250 °C |
| vicat | | ISO306/B | 250 °C |
| | ISO3146 | 265 °C |
| | ISO75-2/A | 250 °C |
| vicat | | ISO306/B | 255 °C |
| | ISO3146 | 265 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.