POM HOSTAFORM® MT12U01
39
- Properties:AntisolventantioxidantImpact resistanceAntichemicalLow friction coefficient
- Usages:Fitness equipmentAutomotive ApplicationsThin walled productsmedical treatmentNursing suppliesThin walled components
Compare
View PricesTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Water absorption rate | ISO62 | 0.65 % | |
| Shrinkage rate | ISO294-4 | 1.8 % | |
| ISO294-4 | 2.0 % | ||
| density | ISO1183 | 1.41 g/cm³ | |
| Melt volume flow rate | ISO1133 | 12.0 cm3/10min |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Nominal tensile fracture strain | ISO527-2/1A/50 | 25 % | |
| Tensile strain | ISO527-2/1A/50 | 9.0 % | |
| Tensile stress | ISO527-2/1A/50 | 65.0 Mpa | |
| Tensile modulus | ISO527-2/1A/1 | 2900 Mpa | |
| TensileCreepModule | ISO899-1 | 2500 Mpa | |
| Tensile creep modulus | ISO899-1 | 1300 Mpa | |
| Flexural modulus | ISO178 | 2800 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of simply supported beam without notch | ISO179/1eU | 150 kJ/m² | |
| ISO179/1eU | 140 kJ/m² | ||
| Charpy Notched Impact Strength | ISO179/1eA | 6.0 kJ/m² | |
| ISO179/1eA | 6.0 kJ/m² |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melting temperature | ISO11357-3 | 166 °C | |
| ISO75-2/A | 106 °C | ||
| ISO11359-2 | 1.1E-04 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.