POM MT12U01 CELANESE GERMANY
HOSTAFORM®
Fitness equipment、Automotive Applications、Thin walled products、medical treatment、Nursing supplies、Thin walled components
Antisolvent、antioxidant、Impact resistance、Antichemical、Low friction coefficient
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | CELANESE GERMANY/MT12U01 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO179/1eA | 6.0 kJ/m² |
| -30°C | ISO179/1eA | 6.0 kJ/m² | |
| Impact strength of simply supported beam without notch | 23°C | ISO179/1eU | 150 kJ/m² |
| -30°C | ISO179/1eU | 140 kJ/m² |
| Mechanical properties | Test Condition | Test Method | CELANESE GERMANY/MT12U01 |
|---|---|---|---|
| Nominal tensile fracture strain | ISO527-2/1A/50 | 25 % | |
| Tensile strain | 屈服 | ISO527-2/1A/50 | 9.0 % |
| Flexural modulus | 23°C | ISO178 | 2800 Mpa |
| TensileCreepModule | 1hr | ISO899-1 | 2500 Mpa |
| Tensile stress | 屈服 | ISO527-2/1A/50 | 65.0 Mpa |
| Tensile modulus | ISO527-2/1A/1 | 2900 Mpa | |
| Tensile creep modulus | 1000hr | ISO899-1 | 1300 Mpa |
| physical property | Test Condition | Test Method | CELANESE GERMANY/MT12U01 |
|---|---|---|---|
| Shrinkage rate | TD | ISO294-4 | 1.8 % |
| Water absorption rate | 饱和,23°C | ISO62 | 0.65 % |
| Shrinkage rate | MD | ISO294-4 | 2.0 % |
| Melt volume flow rate | 190°C/2.16kg | ISO1133 | 12.0 cm3/10min |
| density | ISO1183 | 1.41 g/cm³ |
| Thermal performance | Test Condition | Test Method | CELANESE GERMANY/MT12U01 |
|---|---|---|---|
| 1.8MPa,未退火 | ISO75-2/A | 106 °C | |
| MD | ISO11359-2 | 1.1E-04 cm/cm/°C | |
| melting temperature | ISO11357-3 | 166 °C |