Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D792 | 1.14 g/cm³ |
| Water absorption rate | | ASTM D570 | 0.30 % |
| Water absorption rate | Saturation | ASTM D570 | 6.0 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | M-Scale | ASTM D785 | 85 |
| Rockwell hardness | R-Scale | ASTM D785 | 120 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | HB |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| limiting pv value | | 内部方法 | 0.210 MPa·m/s |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| coefficient of friction | Steel - Static | 内部方法 | 0.14 |
| Wear factor | | ASTM D3702 | 180 10^-8mm³/N·m |
| Tensile modulus | | ASTM D638 | 3210 MPa |
| tensile strength | Ultimate | ASTM D638 | 68.3 MPa |
| elongation | Break | ASTM D638 | 50 % |
| Flexural modulus | | ASTM D790 | 3620 MPa |
| bending strength | Yield | ASTM D790 | 103 MPa |
| Compression Modulus | | ASTM D695 | 2280 MPa |
| compressive strength | | ASTM D695 | 93.1 MPa |
| shear strength | | ASTM D732 | 64.1 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTM D256A | 80 J/m |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ASTM D648 | 93.3 °C |
| Maximum operating temperature LongTerm, Air | | | 104 °C |
| Crystallization peak temperature | | ASTM D3418 | 216 °C |
| Linear coefficient of thermal expansion | | ASTME831 | 1E-04 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.