PA6 Quadrant EPP Nylatron® LFG Nylon Mitsubishi Chemical Advanced Materials
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Mitsubishi Chemical Advanced Materials/Quadrant EPP Nylatron® LFG Nylon |
|---|---|---|---|
| Impact strength of cantilever beam gap | ASTM D256A | 80 J/m |
| Supplementary Information | Test Condition | Test Method | Mitsubishi Chemical Advanced Materials/Quadrant EPP Nylatron® LFG Nylon |
|---|---|---|---|
| limiting pv value | 内部方法 | 0.210 MPa·m/s |
| hardness | Test Condition | Test Method | Mitsubishi Chemical Advanced Materials/Quadrant EPP Nylatron® LFG Nylon |
|---|---|---|---|
| Rockwell hardness | M级 | ASTM D785 | 85 |
| R级 | ASTM D785 | 120 |
| Mechanical properties | Test Condition | Test Method | Mitsubishi Chemical Advanced Materials/Quadrant EPP Nylatron® LFG Nylon |
|---|---|---|---|
| tensile strength | 极限 | ASTM D638 | 68.3 MPa |
| elongation | 断裂 | ASTM D638 | 50 % |
| bending strength | 屈服 | ASTM D790 | 103 MPa |
| compressive strength | 10%应变 | ASTM D695 | 93.1 MPa |
| Tensile modulus | ASTM D638 | 3210 MPa | |
| Flexural modulus | ASTM D790 | 3620 MPa | |
| Compression Modulus | ASTM D695 | 2280 MPa | |
| Wear factor | ASTM D3702 | 180 10^-8mm³/N·m | |
| coefficient of friction | 与钢-静态 | 内部方法 | 0.14 |
| shear strength | ASTM D732 | 64.1 MPa |
| flammability | Test Condition | Test Method | Mitsubishi Chemical Advanced Materials/Quadrant EPP Nylatron® LFG Nylon |
|---|---|---|---|
| UL flame retardant rating | 3.2mm | UL 94 | HB |
| physical property | Test Condition | Test Method | Mitsubishi Chemical Advanced Materials/Quadrant EPP Nylatron® LFG Nylon |
|---|---|---|---|
| Water absorption rate | 饱和 | ASTM D570 | 6.0 % |
| 24hr | ASTM D570 | 0.30 % | |
| density | ASTM D792 | 1.14 g/cm³ |
| Thermal performance | Test Condition | Test Method | Mitsubishi Chemical Advanced Materials/Quadrant EPP Nylatron® LFG Nylon |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648 | 93.3 °C |
| Crystallization peak temperature | DSC | ASTM D3418 | 216 °C |
| Linear coefficient of thermal expansion | MD2：-40到149°C | ASTME831 | 1E-04 cm/cm/°C |
| Maximum operating temperature LongTerm, Air | 104 °C |