| physical property | Test Condition | Test Method | Test Result |
|---|
| melt mass-flow rate | | ASTM D1238 | 22 g/10min |
| melt mass-flow rate | | ISO 1133 | 2.2 g/10min |
| density | | ASTM D792 | 1.04 g/cm³ |
| density | | ISO 1183 | 1.04 g/cm³ |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | ASTM D785 | 110 |
| Rockwell hardness | | ISO 2039-2 | 110 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | HB |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | | ASTM D638 | 43 Mpa |
| tensile strength | | ISO 527-2 | 47.0 Mpa |
| bending strength | | ISO 178 | 73 Mpa |
| Flexural modulus | | ISO 178 | 2550 Mpa |
| Flexural modulus | | ASTM D790 | 26000 kg/cm2 |
| bending strength | | ASTM D790 | 830 kg/cm2 |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTM D256 | 220 J/m |
| Impact strength of cantilever beam gap | | ISO 180 | 25 k/Jm2 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ISO 75-2/A | 86.0 °C |
| Heat distortion temperature | | ASTM D648 | 92.0 °C |
| vicat | | ISO 306/A | 93 °C |
| vicat | | ASTM D15253 | 93 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.