Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
ABS AG15A1-H FCFC TAIWAN
TAIRILAC®
calculator、Clock housing、Phone、suitcase、Toy、Sound enclosure
High gloss、Moderate impact、Universal level
TDS
Processing
MSDS
UL
RoHS
SVHC
PSC
TDS
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | FCFC TAIWAN/AG15A1-H |
|---|---|---|---|
| Impact strength of cantilever beam gap | 23°C,6.35mm | ASTM D256 | 220 J/m |
| 23°C,4.00mm | ISO 180 | 25 k/Jm2 |
| hardness | Test Condition | Test Method | FCFC TAIWAN/AG15A1-H |
|---|---|---|---|
| Rockwell hardness | R计秤,23°C | ASTM D785 | 110 |
| R计秤,23°C | ISO 2039-2 | 110 |
| Mechanical properties | Test Condition | Test Method | FCFC TAIWAN/AG15A1-H |
|---|---|---|---|
| bending strength | 23°C | ASTM D790 | 830 kg/cm2 |
| 23°C | ISO 178 | 73 Mpa | |
| tensile strength | 屈服,23°C | ISO 527-2 | 47.0 Mpa |
| Flexural modulus | 23°C | ISO 178 | 2550 Mpa |
| 23°C | ASTM D790 | 26000 kg/cm2 | |
| tensile strength | 23°C | ASTM D638 | 43 Mpa |
| flammability | Test Condition | Test Method | FCFC TAIWAN/AG15A1-H |
|---|---|---|---|
| UL flame retardant rating | 1.5mm | UL 94 | HB |
| physical property | Test Condition | Test Method | FCFC TAIWAN/AG15A1-H |
|---|---|---|---|
| density | 23°C | ISO 1183 | 1.04 g/cm³ |
| melt mass-flow rate | 200°C/5.0kg | ISO 1133 | 2.2 g/10min |
| density | ASTM D792 | 1.04 g/cm³ | |
| melt mass-flow rate | 220°C/10.0kg | ASTM D1238 | 22 g/10min |
| Thermal performance | Test Condition | Test Method | FCFC TAIWAN/AG15A1-H |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,Annealed,6.35mm，HDT | ASTM D648 | 92.0 °C |
| vicat | ASTM D15253 | 93 °C | |
| ISO 306/A | 93 °C | ||
| Heat distortion temperature | 1.8MPa,Unannealed,6.35mm，HDT | ISO 75-2/A | 86.0 °C |